Título en portugués
Misturas de poliestireno e poliéster lÃquido-cristalino.
Palabras clave en portugués
Análise térmica
Blendas
Compatibilização
Microscopia
PolÃmeros (Materiais)
Resumen en portugués
PolÃmeros lÃquido-cristalinos (LCPs) e poliestirenos comerciais são imiscÃveis. A literatura relata melhoria na miscibilidade dessas blendas através da utilização de polÃmeros modificados. Misturas de polÃmeros com baixa massa molar são mais miscÃveis do que blendas similares com polÃmeros de alta massa molar. Neste trabalho, blendas de poliestireno sintetizado com baixa massa molar (Mv = 11000 e 70000 g/mol) e poliestireno comercial (Mv = 223000 g/mol) e polÃmero lÃquidocristalino termotrópico sintetizado, poli(metil-1,4-dioxifenileno 4,4'-dicarbonil-1,10- dibenzoil-oxi-decano) (Mn = 9500 g/mol, Mw = 24000 g/mol, Mw/Mn = 2,5), foram preparadas por solubilização em clorofórmio e por coprecipitação. A ocorrência ou não da miscibilidade nas amostras foram estudadas através da viscosimetria, de calorimetria exploratória diferencial (DSC) e análise térmica dinâmico-mecânica (DMTA). Os resultados obtidos foram comparados com as micrografias obtidas por microscopia eletrônica de varredura (MEV). As análises quantitativas das micrografias MEV das misturas de LCP com PS 11000 g/mol revelaram que os diâmetros das partÃculas de PS variaram de 27 a 52 nanômetros em blendas (PS/LCP) com composição relativa em massa de 70/30, 50/50, 30/70, formando uma estrutura micro-heterogênea. Já as misturas formadas com PS com Mv = 70000 g/mol apresentaram estrutura cocontÃnua para as mesmas composições de blendas, que confirmam a imiscibilidade das mesmas, conforme observado por DSC e DMTA.
Título en inglés
Polystyrene and liquid-crystal polyester mixtures.
Palabras clave en inglés
Blends
Compatibilization
Microscopy
Thermal analysis
Resumen en inglés
Liquid crystal polymers (LCPs) and commercial polystyrene blends are known to be immiscible. The literature reports improvements on miscibility through polymer modification. Mixtures of amorphous isotropic polymers with low molar mass are more miscible than similar blends with high molar mass polymers. In this work, blends of synthesized polystyrenes with low molar masses (Mv = 11000 e 70000 g/mol) and commercial polystyrene (Mv = 223000 g/mol), and synthesized thermotropic liquid crystal polymer poly(methyl-1,4-dioxiphenylene-4,4'-dicarbonyl- 1,10-dibenzoyl-oxydecane), (Mn = 9500 g/mol, Mw = 24000 g/mol, Mw/Mn = 2.5) were prepared by solubilization in chloroform and co-precipitation. The presence or absence of miscibility in the samples were studied by viscometry, differential scanning calorimetry (DSC), dynamic mechanic thermal analysis (DMTA). The results are compared to the morphology observed by scanning electron microscopy (SEM). Quantitative analysis of the micrographs of the blends by SEM showed that the blends with PS 11000 g/mol showed diameters of the PS particles in the range 27-52 nanometers at all compositions, forming a micro-heterogeneous structure. In contrast, the blends formed with PS Mw = 70000 g/mol showed co-continuous structure for the blends, confirming the immiscibility as observed by DSC and DMTA .
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-11-10