Thèse de Doctorat
DOI
https://doi.org/10.11606/T.43.2003.tde-20022014-141304
Document
Auteur
Nom complet
Denis Rezende de Jesus
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2003
Directeur
Jury
Partiti, Carmen Silvia de Moya (Président)
Amaral, Livio
Itri, Rosangela
Larica, Carlos
Petrilli, Helena Maria
Titre en portugais
Estudo das ligas quaternárias Al-Fe-Si-B produzidas por mecanossíntese
Mots-clés en portugais
Espectroscopia do Mössbauer
Mecanossíntese
Resumé en portugais
Este trabalho tem como objetivo a síntese da liga Fe IND.78-X Al IND.X Si IND.9 B IND.13, com o X=0, 10, 20, 30 e 50, através da moagem utilizando para isto um moinho de bolas de alta energia. As técnicas de difração de raios-X, microscopia eletrônica de varredura, SQUID, análise térmica diferencial (DTA) e espectroscopia Mössbauer são utilizadas na verificação da dependência da estrutura e propriedades magnéticas com o tempo de moagem e diferentes concentrações de Al. Com a moagem uma solução sólida com estrutura BCC é formada, com os átomos sendo distribuídos de forma aleatória na rede. O tamanho de grãos descresce rapidamente nos primeiros estágios de moagem e depois, com a continuação da moagem, permanece aproximadamente constante. Os espectros Mössbauer apresentam linhas alargadas, uma característica dos materiais submetidos a moagem, e forma ajustados considerando sítios paramagnéticos, sextetos cristalinos e distribuições Gaussianas de campos hiperfinos. As medidas magnéticas mostram que as ligas possuem propriedades de material magnético mole. A magnetização e a coercividade diminuem com o tempo de moagem, indicando um aumento no número de átomos não-magnéticos em torno do átomo de ferro e a diminuição do tamanho do grão, respectivamente. Com o aumento da concentração de Al, o tamanho do grão da solução sólida tende a diminuir e o sistema perde seu ordenamento magnético. As curvas DTA mostram uma transformação exotérmica associada à cristalização de fases amorfas e ao ordenamento da solução sólida Fe(Al, Si, B) para formar outros compostos. O tratamento térmico dos pós moídos forma os intermetálicos FeAl, FeAl IND.2. As amostras submetidas a tempos de moagem maiores dão origem a fases nanocristalinas e amorfas com alto grau de contaminação pelos componentes de moinho.
Titre en anglais
Study Quaternary Alloys Al-Fe-Si-B Mechanical Synthesis
Mots-clés en anglais
Mechanical synthesis
Mössbauer spectroscopy
Resumé en anglais
The purpose of the present work is the synthesis of Fe IND.78-xAl IND.xSi IND.9B IND.13 alloy, with x=0, 10, 20, 30 and 50, by mechanical alloying in a high energy planetary ball mil. The effect of the milling time and Al content on the structure and magnetic properties has been studied by X-ray diffraction, scanning electron microscopy, SQUID, differential analysis thermal (DTA) and Mossbauer spectroscopy. After milling a Fe-Al-Si-B solid solution with a bcc structure is formed. The atoms are assumed to be randomly distributed in lattice, the grain size decrease dramatically at the early milling stages with further milling to remain relatively stable at the late stages. The Mossbauer spectra show lines broad, a characteristic of milled materials, and were fitted by considering paramagnetic phases, crystalline sextet and Gaussian distributions of hyperfine fields. The magnetic measurements show soft magnetic properties. The magnetization and coactivity decrease with milling time, indicating an increasing number of nonmagnetic atoms around the iron atoms and decrease of grain size, respectively. With increasing Al content, the grain size of the solid solutions decreased, and the system loses its magnetic order. The DTA curves show the exothermic transformation associated to crystallization of amorphous phase and ordering of the Fe(Al,Si,B) solid solutions to form other compounds. The annealing of milled powders form the ordered FeAl and FeAl IND.2 intermetallic. Long milling times resulted in Nano crystalline and amorphous phases highly contaminated by the milling tools.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2014-02-20
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.