Tesis Doctoral
DOI
https://doi.org/10.11606/T.97.2011.tde-27082013-094247
Documento
Autor
Nombre completo
Reny Angela Renzetti
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Lorena, 2011
Director
Tribunal
Sandim, Hugo Ricardo Zschommler (Presidente)
Santos, Dilson Silva dos
Almeida, Luiz Henrique de
Barboza, Miguel Justino Ribeiro
Suzuki, Paulo Atsushi
Título en portugués
Estudo comparativo da recristalização de dois aços de atividade reduzida endurecidos por dispersão de óxidos (9%Cr e 13%Cr)
Palabras clave en portugués
Fusão nuclear
ODS-Eurofer
Propriedades magnéticas
Recristalização
Textura
Resumen en portugués
O crescente interesse em novos métodos para a geração de energia limpa e sustentável contribui para o desenvolvimento de materiais avançados destinados a aplicações estruturais em reatores de fusão nuclear. Os principais resultados obtidos quanto à caracterização microestrutural de dois aços endurecidos por dispersão de óxidos, candidatos potenciais a este tipo de aplicação, são apresentados. Um dos aços contém 9%Cr e o outro 13%Cr (% em massa). Os aços foram laminados até 80% de redução e recozidos até temperaturas próximas a 0,9 Tf, onde Tf é o ponto de fusão. A cinética de amolecimento foi acompanhada por meio de medidas de dureza Vickers em função da temperatura de recozimento e do tempo. Amostras representativas foram caracterizadas via microscopia eletrônica de transmissão e de varredura e por difração de elétrons retroespalhados. As temperaturas das transformações de fases foram determinadas por técnicas como dilatometria e análise térmica diferencial. Curvas de magnetização em função do campo magnético aplicado até 15 kOe foram obtidas para o aço com 9%Cr. Medidas de difração de raios X para determinar a densidade de discordâncias também foram realizadas em amostras representativas do aço com 9%Cr. Os resultados até o momento mostram que o engrossamento microestrutural destes aços só se torna significativo quando o recozimento é feito em temperaturas acima de 0,8 Tf. Em temperaturas mais baixas, ainda no campo ferrítico, a recuperação prevalece e a fração recristalizada é baixa. A resistência destes materiais à recristalização se deve à presença das partículas de óxido de ítrio dispersas na matriz que dificultam a movimentação e o rearranjo das discordâncias e contornos durante sua migração. Por outro lado, partículas grosseiras como as dos carbonetos M23C6 estimulam a recristalização atuando como sítios preferenciais para a nucleação. O recozimento em temperaturas elevadas no campo austenítico resultou no aumento considerável na dureza Vickers e na densidade de discordâncias para o aço com 9%Cr devido à transformação martensítica. No aço com 13%Cr os resultados também sugerem a ocorrência da transformação martensítica.
Título en inglés
Comparative study of the recrystallization of two oxide dispersion strengthened reduced activation (9%Cr and 13%Cr) steels
Palabras clave en inglés
Magnetic properties
Nuclear fusion
ODS-Eurofer
Recrystallization
Texture
Resumen en inglés
There is an increasing interest in the development of new, sustainable, clean and safe sources of energy. In view of these requirements, the development of advanced materials for future nuclear fusion reactors becomes essential. This work investigates the annealing behavior and the microstructural stability of two oxide dispersion strengthened steels with 9%Cr and 13%Cr ODS steels. These materials are potential candidates for structural applications in future fusion reactors. The two ODS steels were cold rolled to 80% thickness reduction. Samples were annealed in vacuum at temperatures of about 0.9 Tm, where Tm is the melting point. The microstructural characterization was performed by Vickers hardness testing, transmission electron microscopy (TEM), scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD) performed by a highresolution SEM. Important temperatures related to the phase transformations were determined with aid of dilatometry and differential thermal analysis (DTA). Magnetization curves as a function of applied magnetic fields up to 15 kOe were obtained for 9%Cr ODSEurofer. X-ray diffraction experiments were also performed on 9%Cr steel to evaluate the dislocation density in several metallurgical conditions. Results show that microstructural coarsening becomes significant when annealing is performed above 0.8 Tm. Below 800°C, static recovery is the main softening mechanism of these steels and the volume fraction of recrystallized grains is quite low. The resistance of these steels to recrystallization can be explained by the strong interaction between boundaries and mobile dislocations with fine particles of Y-based oxides. Contrastingly, coarse M23C6 particles act as preferential nucleation sites through the well-known particle stimulated nucleation (PSN) mechanism. Samples annealed above 800oC (austenitic phase field) display larger dislocation densities in the 9%Cr ODS steel. Results concerning to 13%Cr steel suggest the occurrence of martensitic transformation.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
EMT11003.pdf (27.48 Mbytes)
Fecha de Publicación
2013-08-27
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.