Disertación de Maestría
DOI
10.11606/D.100.2013.tde-08112013-122649
Documento
Autor
Nombre completo
Agatha Cristine Carretero
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2013
Director
Tribunal
Costa, Silgia Aparecida da (Presidente)
Marcicano, João Paulo Pereira
Oliveira, Rodrigo Cardoso de
Título en portugués
Desenvolvimento de fibras têxteis a base de polímeros naturais para aplicações médicas
Palabras clave en portugués
Alginato
Fibras têxteis
Quitosana
Têxteis técnicos
Resumen en portugués
Dentre a grande variedade de polímeros naturais que podem ser aplicados na área médica, a quitosana e o alginato têm sido amplamente destacados. A quitosana é obtida a partir da desacetilação da quitina que é extraída do exoesqueleto de crustáceos, ou seja, de rejeitos da indústria pesqueira. O alginato é um polissacarídeo obtido de algas, muito utilizado na indústria farmacêutica. O objetivo deste trabalho foi a produção de fibras têxteis à base de quitosana, alginato e híbrida (alginato/quitosana) para aplicação na área médica, devido as propriedades de biocompatibilidade, antimicrobiana, cicatrizante, entre outras, presente nesses polímeros. As fibras de quitosana foram preparadas por um gel, dissolvendo a quitosana 2,5% (m/v) em ácido acético 2% (v/v), após a preparação do gel foram extrudadas em uma solução de precipitação contendo sulfato de sódio 0,5M e hidróxido de sódio 1M. As fibras foram produzidas com um gel de alginato a 5% (m/v) através da extrusão em solução de cloreto de cálcio 2% (m/v). As híbridas foram produzidas através da extrusão do gel de alginato em uma solução 0,2% (m/v) de quitosana. Algumas fibras foram produzidas com 2,5 % de glicerol, adicionado diretamente ao gel. As microcopias eletrônicas de varredura (MEV) mostram regularidades ao longo do comprimento e ranhuras laterais nas fibras produzidas. As amostras foram testadas e obtiveram bons valores de absorção de água, chegando a 215% em 30 dias para a fibra híbrida. Quanto a perda de massa, as fibras produzidas com glicerol obtiveram maior degradação. As amostras também foram submetidas a calorimetria exploratória diferencial (DSC) para análise do comportamento térmico. O glicerol foi responsável por deslocar os picos endotérmicos para a direita em relação aquelas sem glicerol, ou seja, em uma temperatura maior, enquanto os picos exotérmicos ocorreram em uma temperatura menor. Nos testes físicos, foi obtido baixos valores de tenacidade e alto título. As fibras são atóxicas e os resultados mostraram a potencialidade do uso desses polímeros na produção de fibras têxteis.
Título en inglés
Development of textile fibers made of natural polymers to be applied in medical area
Palabras clave en inglés
Alginate
Chitosan
Technical textiles
Textile fibers
Resumen en inglés
Among the wide variety of natural polymers that can be applied in medical area, chitosan and alginate have beem widely deployed. Chitosan is obtained from the deacetylation of chitin, wich is extracted from the exoskeleton of shellfish, and is characterized as a reject of fishing industry. The alginate is polysaccharides obtained from algae and have commom use in pharmaceutical industry. The objective of this work is the production of textile fibers based on chitosan, alginate, and hybrid (alginate/chitosan) for application in medical field, because of the properties of biocompatibility, antimicrobial, wound healing capability, among others, present in these polymers. The fibers of chitosan were prepared by a gel, by dissolving the chitosan 2.5% (w/v) in acetic acid 2% (v/v), after preparation of the gel, it was made a extrusion in a precipitating solution containing sodium sulfate 0,5 M and sodium hydroxide 1 M. Other fiber was produced using an alginate gel 5% (w/v) by extrusion in calcium chloride solution 2% (w/v). Hybryd fibers were made by extruded the same alginate gel in a chitosan solution 0.2 % (w/v). Some fibers have been produced with 2.5% (w/v) glycerol added directly to the gel. The electronic microscopy shows regularities along the length of lateral. The samples were tested and showed good values of water absorption, reaching 215% in 30 days for the hybrid fiber. As for weight loss, the fibers produced with glycerol had higher degradation. The samples were also subjected to differential scanning calorimetry (DSC) to analyze thermal behavior. Glycerol was responsible for the endothermic peaks shift to the right in relation of the one without glycerol, occurring in a higher temperature, while the exotermic peaks occurred at a lower temperature. In the physical tests, was obtained low values of tenacity and high yarn number. The fibers are nontoxic and the results showed the potential use of these polymers in the production of textile fibers.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2015-02-12
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.