Tesis Doctoral
DOI
10.11606/T.102.2017.tde-23012017-100027
Documento
Autor
Nombre completo
Joseph Salem Barbar
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2016
Director
Tribunal
Rossignolo, João Adriano (Presidente)
Ferreira, Fernanda Giannotti da Silva
Fiorelli, Juliano
Pablos, Javier Mazariegos
Peruzzi, Antônio de Paulo
Título en portugués
Influência do teor de ar incorporado no desempenho de concretos com diferentes teores de agregados
Palabras clave en portugués
Carbonatação
Concreto com ar incorporado
Concreto leve
Condutividade térmica
Micro-CT
Resumen en portugués
A utilização de aditivos incorporadores de ar em concretos é uma prática comum na construção civil e sua aplicação influencia significativamente diversas propriedades do concreto no estado fresco e endurecido. O objetivo deste estudo foi avaliar a influência do teor de ar incorporado, por meio de aditivo, no desempenho de concretos com diferentes teores de agregados. O programa experimental incluiu avaliação da eficiência de aditivos na incorporação de ar em pastas de cimento, análise microestrutural e ensaios para determinação de propriedades físicas, mecânicas e de durabilidade de concretos com diferentes teores de ar e agregados. No estado fresco, foram realizados ensaios para determinação do teor de ar, massa específica e abatimento. No estado endurecido foram realizados ensaios de massa específica, absorção, resistência à compressão, módulo de elasticidade, velocidade de propagação da onda ultrassônica, carbonatação acelerada e condutividade térmica. Utilizando Microtomografia Computadorizada de Raios-X (Micro-CT) foram dimensionados e quantificados os poros presentes nas amostras dos concretos, bem como determinadas suas porosidades. Os concretos com ar incorporado apresentaram redução na resistência mecânica. Os concretos com menores teores de agregados apresentaram menor resistência mecânica, menor velocidade da frente de carbonatação e menor condutividade térmica. De acordo com os resultados obtidos, pode-se concluir que o aditivo a base de resinas sintéticas foi mais eficiente na incorporação de ar; maiores teores de ar implicam em variabilidade nos resultados de ensaios de resistência à compressão e módulo de elasticidade; os concretos com maiores teores de agregados apresentaram maior velocidade da frente de carbonatação, para mesmos teores de ar incorporado; a condutividade térmica é inversamente proporcional ao teor de ar incorporado no concreto, e quanto menor o teor de agregados, menor a condutividade térmica; o aumento do teor de ar no concreto promove aumento no diâmetro equivalente dos poros e redução da incidência de poros esféricos.
Título en inglés
The influence of air entrained content in concrete performance with different aggregate contents
Palabras clave en inglés
Air entrained concrete
Carbonation
Lightweight concrete
Micro-CT
Thermal conductivity
Resumen en inglés
The use of entraining air additives in concrete is a common practice in construction and its application influences several concrete properties in the fresh and hardened state. The aim of this study was evaluate the influence of air entrained content, by additive, in concrete performance with different aggregate contents. The experimental program included the evaluation of additives effectiveness of air entrainment in cement pastes, microstructural analysis and the concretes physical and mechanical properties and durability, with different levels of entrained air and aggregates. Tests were performed in fresh to determine the air content, density and slump. In hardened concrete, density, absorption, compressive strength, elastic modulus, ultrasonic pulse velocity, accelerated carbonation and thermal conductivity tests were performed. By computed X-ray microtomography, the pores present in the concrete samples were sized and quantified and determined the concretes porosities. The air entrained concrete presented decrease in mechanical strength. Concretes with lower aggregate levels presented lower mechanical strength, carbonation speed and thermal conductivity. According to the results, it can be concluded that the synthetic resins base additive was more efficient in air entrainment; larger air content implies variability in the results of the compressive strength and elastic modulus tests; concrete with higher aggregate levels presented higher carbonation speed, for the same entrained air content; thermal conductivity is inversely proportional to the air entrained content in concrete, and as lower was the aggregate content, lower was the thermal conductivity; the increase of air content in concrete promotes increase in the pores diameter and reduction of the incidence of spherical pores.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-01-24
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.