Disertación de Maestría
DOI
10.11606/D.11.2001.tde-13122001-114259
Documento
Autor
Nombre completo
Maria de Lourdes Aparecida Prudente Soffner
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Piracicaba, 2001
Director
Tribunal
Silva Junior, Francides Gomes da (Presidente)
Nolasco, Adriana Maria
Sansigolo, Claudio Angeli
Título en portugués
Produção de polpa celulósica a partir de engaço de bananeira.
Palabras clave en portugués
engaço de bananeira
polpa de celulose
polpação
resíduo agrícola.
Resumen en portugués
O engaço de bananeira, suporte que sustenta o cacho de bananas, normalmente é descartado após a colheita da fruta, seja nas casas de embalagens (packing houses) ou em centros distribuidores, onde é considerado verdadeiro resíduo pelo grande volume gerado e por não ser aproveitado. Por essa razão e por constituir-se em material fibroso, o engaço foi avaliado para produção de polpa celulósica. O engaço in natura apresenta cerca de 93% de umidade e células de parênquima em abundância; em termos de composição química, o engaço apresenta 7,4% de lignina, 47,8% de extrativos totais, e 47,6% de holocelulose. Nesta pesquisa, a performance do engaço como matéria-prima para produção de polpa celulósica foi avaliada, usando o CaO como fonte álcali. Foram utilizadas lavagem e pré-extração aquosa (100 ºC, por 100 minutos) como pré-processos com o propósito de reduzir a grande quantidade de extrativos no bagaço do engaço de bananeira. O bagaço original e os materiais obtidos após os pré-processos foram submetidos à polpação com CaO com 8, 10, 12 e 14% de CaO, à temperatura de 120 ºC por 120 minutos em digestor rotativo. Para comparação foi utilizado o processo soda de polpação, sob as mesmas condições, usando-se 12% de NaOH como carga alcalina. Os resultados mostraram que a aplicação da lavagem e pré-extração aquosa ocasionaram a redução de cerca de 40% da massa inicial do bagaço. Considerando-se as condições de polpação e também a composição química do engaço de bananeira, os pré-processos avaliados não apresentaram um significativo efeito no processo de cozimento. Para a polpação do engaço, o processo de polpação cal pode ser considerado uma alternativa técnica para produção de polpa celulósica, apresentando níveis de deslignificação similar ao do processo de polpação soda.
Título en inglés
Pulp production from banana stem.
Palabras clave en inglés
agricola residue
banana stem
pulp
pulping
Resumen en inglés
The banana stem, grain stalk that supports the banana fruits, is normally discarded after the fruit harvesting, either in the 'packing house' or in the delivering centers, where it is considered a residue due to the great volume generated. For this reason and for being a fibrous material, stem was evaluated for pulp production. The stem in natura presents 93 % of humidity and parenchymatic cells in abundance; in terms of chemical composition the stem presents 7,4% of lignin, 47,0 % of total extractives and 45,6% of holocelullose. In this research, the performance of the stem as raw material for pulp production was evaluated, using the CaO as an alkali source. Washing and aqueous pre-extraction (100 ºC and 100 minutes) were considered as a pre-process in order to reduce the amount of extractives on the banana stem bagasse; the original bagasse and the materials obtained after the pre-processes were submitted to the CaO pulping with 8, 10, 12 and 14 % of CaO, at 120 ºC temperature during 120 minutes in rotating digester. For comparison, a soda cooking was carried out, under the same conditions using 12% of NaOH as alkaline charge. The results showed that the aplication of washing and aqueous pre-extraction caused a reduction of about 40% in the initial mass of bagasse. Considering the pulping conditions and also the chemical composition of the banana stem bagasse the pre-process evaluated did not show a significant effect on the cooking process itself. For the banana stem pulping, a CaO process can be considered a technical alternative for pulp production, with delignification rates similar to the NaOH process.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
soffner.pdf (2.72 Mbytes)
Fecha de Publicación
2002-05-17
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.