Master's Dissertation
DOI
Document
Author
Full name
Ugo Leandro Belini
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
Piracicaba, 2007
Supervisor
Committee
Tomazello Filho, Mario (President)
Bortoletto Junior, Geraldo
Oliveira, José Tarcisio da Silva
Title in Portuguese
Caracterização e alterações na estrutura anatômica da madeira do Eucalyptus grandis em três condições de desfibramento e efeito nas propriedades tecnológicas de painéis MDF
Keywords in Portuguese
Anatomia vegetal
Chapa de fibra
Desfibramento
Eucalipto
Madeira
Abstract in Portuguese
Constata-se, atualmente, uma grande demanda de crescimento na produção de painéis MDF de madeira de eucalipto em relação à do pinus, comumente utilizada na indústria. Pelo exposto, o presente trabalho teve como objetivo caracterizar os componentes morfológicos da madeira de cavacos de Eucalyptus grandis, “in natura” e submetidas a três condições diferentes de desfibramento (tempo, pressão e energia), sendo denominadas de condição intermediária, de menor e de maior intensidade de refino (A, B e C, respectivamente). As características tecnológicas das chapas MDF obtidas para as três condições de desfibramento foram, da mesma forma, analisadas segundo a norma NBR 15316. No desenvolvimento do trabalho foram coletados para as três condições de desfibramento, em toda a cadeia produtiva do painel MDF: cavacos de madeira, material lenhoso desfibrado e painéis MDF final em escala industrial e laboratorial. Os cavacos de madeira foram caracterizados com respeito a sua estrutura microscópica; o material lenhoso desfibrado nas 3 condições foi avaliado através do seu fracionamento em peneiras seguindo-se a classificação morfológica e a caracterização microscópica dos componentes celulares de cada fração. Os resultados mostraram que os cavacos de madeira coletados no silo da unidade fabril apresentaram-se homogêneos nas 3 pré-condições avaliadas e não exerceram qualquer influência nos tratamentos. A condição de desfibramento mais branda induziu a formação de feixes de fibra e manutenção de vasos e parênquima com as fibras apresentando maior comprimento médio. A condição de desfibramento mais drástica induziu o rompimento da parede das fibras, com polpa apresentando fibras de menor comprimento e com baixa freqüência de vasos e de parênquima. As características de coloração foram observadas, sendo que a massa de fibras mais escura foi decorrente da alta pressão, maior tempo e mais energia de refinação aplicada. Os painéis MDF obtidos na condição mais branda apresentaram maior resistência ao arranque de parafuso, ao contrário dos painéis MDF confeccionados com polpa da condição de desfibramento mais drástica mostrando menores propriedades mecânicas de resistência à tração perpendicular e superficial e maiores valores de inchamento e de absorção. Os resultados do trabalho evidenciam a importância das variáveis de produção relacionadas com os tratamentos da madeira e do material fibroso nas propriedades tecnológicas dos painéis MDF de eucalipto.
Title in English
Characterization and anatomical structure alterations of Eucalyptus grandis wood in three refining conditions and effect in technological properties of MDF panels
Keywords in English
Eucalyptus grandis
MDF panel
Medium density fiberboard
Wood anatomy
Wood refining
Abstract in English
Currently is evidenced a great demand of growth in eucalypts MDF panels production in relation with pinus, commonly used in the industry. The present study had the objective to characterize the morphologic components of Eucalyptus grandis wood chips “in natura” submitted in three different refining conditions (time, pressure and energy), named intermediate, smaller and biggest intensity of refining (A, B and C, respectively). The technological characteristics of MDF panels from three refining conditions were analyzed according standard NBR 15316. During this development were collected for three refining conditions, in all the productive chain of the MDF panels: wood chips, wooden dissociated material and panels MDF in industrial and laboratorial scale. The wood chips structure were microscopically characterized; the dissociated wood cells suspended in water of 3 refining conditions were evaluated through its separation in sieves and each fraction of woody material was morphologically classified and microscopically described. The results showed that the wood chips collected in industry storage compartment were homogeneous in the 3 refining preconditions and not influenced the MDF panel's treatments. The softness refining condition induced the shives formation and maintenance of vessels, parenchyma and the longest fibers. The more drastic refining condition induced the fiber cell walls broking, with wood pulp presenting shortest fibers and lower vessels and parenchyma frequency. The coloration characteristics were observed, and the fiber pulp was darker as result of the high pressure, greater time and more refinement energy applied. The MDF panels elaborated by softness refining condition presented greater resistance to screw pull in contrast of panels confectioned with hardness refining condition showing lesser mechanical properties of perpendicular and superficial tensile strength and bigger values of swelling and absorption. The results showed the importance of the variable related production with the wood and pulp wood treatments in technological properties of eucalypts MDF panels.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
UgoBelini.pdf (1.56 Mbytes)
Publishing Date
2007-06-11
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
CeTI-SC/STI
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2021. All rights reserved.