Disertación de Maestría
DOI
https://doi.org/10.11606/D.11.2003.tde-06112003-135906
Documento
Autor
Nombre completo
Fábio Sergio de Almeida
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
Piracicaba, 2003
Director
Tribunal
Silva Junior, Francides Gomes da (Presidente)
Barrichelo, Luiz Ernesto George
Foelkel, Celso Edmundo Bochetti
Título en portugués
Influência da carga alcalina no processo de polpação Lo-Solids® para madeiras de eucalipto.
Palabras clave en portugués
celulose
densidade da madeira
madeira de eucalipto
polpa da madeira
polpação
química da madeira.
Resumen en portugués
O presente trabalho teve por objetivo estudar a influência da carga alcalina no processo de polpação kraft modificado Lo-SolidsÒ para madeiras de eucalipto, considerando parâmetros como rendimento, teor de rejeitos, geração de sólidos e características da polpa tais como número kappa, viscosidade, composição polissacarídica e morfologia de fibras. Híbridos de E. grandis x E. urophylla com 7 anos e densidade básica de 500 e 560kg/m 3 foram avaliados e os cozimentos Lo-Solidsâ foram realizadas aplicando-se álcali ativo (como Na2O) de 13%, 15%, 17%, 19%, 21%, 23%, 25%, 27% e sulfidez de 30%. O delineamento experimental adotado foi o inteiramente casualizado. Os resultados obtidos indicam que variando a carga alcalina no processo de polpação é possível obter polpa não branqueada apresentando valores de kappa de 8 a 30, rendimento depurado de 46 a 53%, viscosidade de 10 a 80 cP, solubilidade em NaOH 5% (S5) de 7 a 13%, teor de pentosanas de 11 a 16% e ácidos hexenurônicos de 10 a 65 µ mol/g. O aumento da carga alcalina nos cozimentos proporcionou maior geração de finos e, consequentemente, menor comprimento médio ponderado de fibras e espessura de parede. Embora os materiais estudados apresentassem diferentes densidade básica, os resultados de polpação foram semelhantes indicando que ambas matérias-primas podem ser empregadas na obtenção de polpa celulósica utilizando o processo de cozimento Lo-Solids®, o qual não se mostrou sensível a densidade básica, o que possivelmente está associado a boa impregnação dos cavacos correspondente à etapa de impregnação. O híbrido de maior densidade produziu polpa com fibras de maior espessura de parede, maior coarseness e menor número de fibras por grama que o híbrido de menor densidade básica. As análises do licor negro mostraram que o de pH, o álcali efetivo residual e o teor de sólidos dissolvidos apresentam maiores valores para dosagens de álcali também superiores, porém observa-se um perfil uniforme para essas variáveis, evidenciando a homogeneidade do processo de polpação Lo-SolidsÒ.
Título en inglés
The influence of alkali charge on lo-solidsâ â pulping process for eucalyptus woods.
Palabras clave en inglés
basic density of wood
cellulose
eucalyptus wood
pulp of wood
pulping
wood chemistry.
Resumen en inglés
The main objective of this work was to study the influence of the alkali charge on Lo-Solidsâ modified kraft pulping process for eucalyptus, considering parameters as yield, rejects content, total dissolved solids materials and the pulp characteristics as kappa number, viscosity, carbohydrate composition and fibers dimensions. Woods from hybrids of Eucalyptus grandis x Eucalyptus urophylla 7 years old and presented basic density of 0,499 and 0,559g/cm 3 were evaluated and the pulping process was conducted applying active alkali charge (as Na2O) of 13%, 15%, 17%, 19%, 21%, 23%, 24%, 25%, 27% and sulfidity of 30%. The results showed that varying the alkali charge is possible to obtain unbleached pulp with kappa number from 8 to 30, pulp yield from 46 to 53%, viscosity from 10 to 80cP, alkali solubility (S5) from 7 to 13%, pentosans content from 11 to 16% and hexenuronic acids content from 10 to 65µmol/g. It was verified that the higher is the alkali charge the higher is the fines generation leading to a decreased of fiber length and the cell wall thickness. Although the hybrids studied presented different wood basic density, the pulping results obtained were not different showing that both raw-materials could be used to pulp production with Lo-SolidsÒ pulping process, which seems not to be so affect by wood basic density. The pulp obtained from hybrid with higher basic density showed higher cell wall thickness, higher fiber coarseness and lower number of fibers per gram than the hybrid with lower basic density. The analysis of black liquor showed that the pH, the effective residual alkali and the total dissolved solids materials increased when the alkali charge applied is higher too, however a uniform profile is noted for these variables, showing the homogeneity of Lo-SolidsÒ pulping process.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
fabio.pdf (377.23 Kbytes)
Fecha de Publicación
2004-08-13
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.