Disertación de Maestría
DOI
https://doi.org/10.11606/D.18.2018.tde-14062018-144401
Documento
Autor
Nombre completo
Janice Mesquita Teodoro
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1999
Director
Tribunal
Bueno, Benedito de Souza (Presidente)
Consoli, Nilo Cesar
Nogueira, João Baptista
Título en portugués
Resistência ao cisalhamento de solos reforçados com fibras plásticas
Palabras clave en portugués
Compósitos de solos
Fibras de polipropileno
Fibras plásticas
Reforço de solo
Resumen en portugués
Este trabalho aborda o comportamento de dois solos (uma argila e uma areia), reforçados com fibras plásticas de polipropileno. Os solos foram compactados no teor de umidade ótimo e peso específico seco máximo e foram misturados com fibras de diferentes teores e comprimentos. Os resultados dos ensaios de compressão simples foram usados para selecionar os teores e comprimentos ótimos de fibras. Os resultados mostraram que a resistência do solo arenoso cresceu com o aumento do teor e comprimento das fibras e o solo argiloso apresentou acréscimo de resistência, com o aumento do teor até o comprimento de fibra de 10 mm. As curvas tensão-deformação dos ensaios triaxiais, para solos com e sem reforço foram similares, com uma resistência de pico definida e pequena redução de queda de tensão pós pico. As amostras de solo arenoso apresentaram considerável aumento de resistência, com o aumento do teor e comprimento das fibras. Pequenos painéis, fabricados com o solo argiloso (300 x 300 x 100) mm, mostraram que a presença da fibra pode reduzir a magnitude das trincas quando comparados com o solo sem reforço.
Título en inglés
not available
Palabras clave en inglés
Plastic fibers
Polypropylene fibers
Soil reinforcement
Soils composites
Resumen en inglés
This work presents the behavior of two soils (clay and sandy) reinforced with polypropylene plastic fibers. The soils were compacted at the optimum moisture content and maximum dry unit weight and were mixed with fibers of different lengths and contents. Unconfined compressive tests results were used to select the optimum fiber length and content. The results showed that the granular soil strength increased with increasing fiber length and content. The cohesive soil, on the other hand, showed strength up to fiber length of 10 mm. Stress - strain curves from triaxial tests for both reinforced and unreinforced cohesive soil were similar with a defined peak strength and small post peak reduction. Granular soil samples presented considerable strength increases with the increases of length and fiber content. Small panels fabricated with the reinforced cohesive soil (300 x 300 x 100) mm, showed that the presence of fiber can reduce crack magnitude when compared with the unreinforced soil.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-06-14
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.