Disertación de Maestría
DOI
10.11606/D.18.2010.tde-06042010-105920
Documento
Autor
Nombre completo
Ellen Kellen Bellucio
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2010
Director
Tribunal
El Debs, Mounir Khalil (Presidente)
Bastos, Paulo Sérgio dos Santos
Rossignolo, João Adriano
Título en portugués
Influência da rugosidade superficial e o uso de novos tipos de fibras em almofadas de argamassa para ligações de concreto pré-moldado
Palabras clave en portugués
Almofadas de apoio
Estruturas de concreto pré-moldado
Ligações
Resumen en portugués
Este trabalho apresenta o estudo de uma argamassa modificada para ser utilizada como almofada de apoio em ligações entre elementos de concreto pré-moldado. Esta argamassa é composta de cimento e areia, com a adição de látex estireno-butadieno (SB), agregado leve (vermiculita) e fibras curtas (polipropileno, vidro e PVA). As pesquisas anteriores mostraram que este compósito apresentou uma boa resistência à compressão e baixo módulo de elasticidade. O objetivo desta pesquisa é dar continuidade dos estudos anteriores analisando a influência da rugosidade superficial nas almofadas, introduzida para aumentar a sua deformabilidade e testar diferentes tipos de fibras. A rugosidade é analisada comparando placas com ambos os lados lisos, um lado liso e outro rugoso e ambos os lados rugosos. Foram estudadas dois tipos de fibras de polipropileno de 10 mm de comprimento - uma com 12 'mü'm e outra com 180 'mü'm de diâmetro. Nesta pesquisa foram realizados ensaios de caracterização do compósito (compressão simples, tração por compressão diametral e módulo de elasticidade) e ensaios em placas (compressão centrada monotônica e cíclica, força concentrada e flexão). Os resultados de caracterização apontam um bom comportamento do compósito, com resistência à compressão de 41 MPa e módulo de elasticidade de 12,8 GPa. Os ensaios de placas mostram melhores resultados para fibras de 12 'mü'm de diâmetro em função de: a) uma redução de 30% da rigidez nos ensaios monotônicos em relação a uma argamassa de referência, b) melhor capacidade de absorção de carga no ensaio de força concentrada e c) no ensaio de flexão, um índice de tenacidade 40% maior quando comparadas com os outros traços estudados. Na análise da rugosidade superficial, o melhor resultado é com rugosidade em ambos os lados da placa, sendo que nos ensaios de carregamento monotônico e cíclico houve uma redução de até 30% na rigidez e um aumento do afundamento acumulado de mais de 120% em relação às placas com ambos os lados lisos.
Título en inglés
Influence of surface roughness and the use of new types of fiber in bearing pads of cement-based material for precast concrete connections
Palabras clave en inglés
Bearing pads
Connections
Precast concrete structures
Resumen en inglés
This paper presents the study of a mortar modified to be used as a bearing pad connections between precast concrete elements. This mortar is composed of cement and sand, with the addition of styrene-butadiene latex (SB), lightweight aggregate (vermiculite) and short fibers (polypropylene, glass and PVA). Previous research showed that this composite presents good compressive strength and low modulus of elasticity. The objective of this research is to continue the previous studies, analyzing the influence of surface roughness on the pads, introduced to increase its deformability, and test other types of fibers. The roughness is analyzed by comparing bearing pads with both smooth sides, one side smooth and other rough and rough both sides. Two types of polypropylene fibers of 10 mm in length - one with 12 'mü'm and another with 180 'mü'm in diameter are studies. In this research, test were carry out to characterize the composite (compressive strength, tensile strength by diametral compression and modulus of elasticity) and test on bearing pads (uniform compressive load - monotonic and cyclic, concentrated load and bending). The results on cylindrical samples to characterize the composite indicate a good behavior, the compressive strength of 41 MPa and modulus of elasticity of 12.8 GPa. The test bearing pads presents the best results for fibers of 12 'mü'm of diameter in terms of: a) a 30% reduction of stiffness in the monotonic tests in relation to a reference mortar, b) the best ability to absorb the load test concentrated load and c) the bending test, an index of toughness 40% higher when compared with the other mixture studied. Regarding surface roughness analysis, the best result is with roughness on both sides of the bearing pads, and tests of monotonic and cyclic loading are reduced by 30% in stiffness and an increase in deformation accumulated more than 120% bearing pads regarding with both sides smooth.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2010-04-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.