Thèse de Doctorat
DOI
10.11606/T.18.2016.tde-18042016-113235
Document
Auteur
Nom complet
Tatiana Bittencourt Dumêt
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2003
Directeur
Jury
Pinheiro, Libânio Miranda (Président)
Ducatti, Vitor Antonio
El Debs, Ana Lúcia Homce de Cresce
El Debs, Mounir Khalil
Figueiredo, Antonio Domingues de
Titre en portugais
Aderência de cordoalhas em concretos de alta resistência com e sem fibras de aço
Mots-clés en portugais
Aderência
Concreto
Concreto de alta resistência
Concreto protendido
Cordoalhas
Fibras de aço
Pré-tração
Resumé en portugais
Este trabalho apresenta os resultados das investigações teórica e experimental sobre a aderência de cordoalhas pré-tracionadas, em concretos de alta resistência com e sem fibras de aço. Foram utilizadas cordoalhas de sete fios com Φp 12,7 mm e fibras de aço curtas, com ganchos nas extremidades (DRAMIX) e fator de forma 1/d=45. Foram realizados dois tipos de ensaios: arrancamento e flexão em viga. Os parâmetros estudados foram: comprimento de ancoragem (5Φp, 7Φp e 15Φp), volume de fibra (zero, 40 kg/m3 e 60 kg/m3 e grau de protensão (zero e 0,8fptk). O concreto apresentou resistências à compressão de 50 MPa no momento da transferência da protensão e 68 MPa na data de ensaio, aproximadamente. Os resultados dos dois tipos de ensaio foram analisados e comparados com as prescrições normativas da NBR 6118 (2001), da FIB Bulletin 1 (1999) e do ACI 318 (2002), onde verificou-se que as prescrições se encontram a favor da segurança. A conclusão principal resultante desta pesquisa foi que a utilização de fibras com 40 kg/'m3 por metro quadrado não influi na aderência. Já para um volume de fibra de 60 kg/'m3 por metro quadrado há um ganho de aproximadamente 28% na aderência, em relação aos concretos sem fibras de aço, nos ensaios de arrancamento. Para as vigas, não houve ganho de aderência para os volumes de fibra utilizados, nem na determinação do comprimento de transferência, nem na do comprimento de ancoragem necessário.
Titre en anglais
Bond of strands embedded in plain and steel fiber reinforced high strength concrete
Mots-clés en anglais
Bond
Concrete
High-strength concrete
Prestressed concrete
Pretensioned concrete
Steel fibers
Strands
Resumé en anglais
This study presents the results of a theoretical and an experimental investigation of the bond of pretensioned strands embedded in plain and steel fiber reinforced high strength concrete. There were used seven wires strands with 12,7 mm diameter and short hooked steel fibers with an aspect ratio of 1/d=45. Two types of tests were carried out to obtain the bond characteristics of the strands: pullout tests and beam under flexure tests. The parameters studied were the volume fraction (0%, 0,51% and 0,76%) of the fibers, and the degree of prestress of the strand (zero and 0,8fptk). The concrete compressive strength was 50 MPa at transfer (3 days of age) and 68 MPa at 28 days of age (test date), approximately. The results were analyzed and compared to the provisions of the following Codes: NBR 6118 (2001) (Brazilian code under public consult), ACI-318 (2002) and FIB-Bulletin 1 (1999). The comparison indicated that the codes give a safe design. The main conclusion of this work was that the use of 0,5% of steel fibers does not influence the bond strength of the strand. The use of 0,76% of steel fibers increases the bond stress in 28% when compared with plain concrete, for the pullout tests. For the beam's tests there was no bond improvement due to the steel fibers, in both case (0,5% and (0,76%), neither for the transfer length nor for the development length.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2016-04-18
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.