Tesis Doctoral
DOI
10.11606/T.18.2018.tde-18052018-202939
Documento
Autor
Nombre completo
Alcebíades Negrão Macêdo
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2000
Director
Tribunal
Calil Junior, Carlito (Presidente)
Ballarin, Adriano Wagner
Dias, Antonio Alves
Proença, Sergio Persival Baroncini
Rodrigues Junior, Manoel Santinho
Título en portugués
Fadiga em emendas dentadas em madeira laminada colada
Palabras clave en portugués
Emendas dentadas
Fadiga
Madeira laminada colada
Resumen en portugués
O objetivo deste trabalho é o estudo da resistência e rigidez das emendas dentadas à fadiga na tração com as finalidades de propor uma metodologia de ensaio e estimar um coeficiente redução da resistência à fadiga na tração das emendas dentadas em relação a madeira maciça, contribuindo para a caracterização destas ligações. Foram utilizadas duas espécies de madeira, Pinus caribea hondurensis e Eucalyptus grandis, e dois tipos de adesivos sendo um industrial à base de fenol-resorcinol e um poliuretano à base de resina de mamona desenvolvido no Instituto de Química de São Carlos. Foram realizados ensaios cíclicos para três níveis de freqüência (1 Hz, 5 Hz e 9 Hz) e três níveis de tensão (90%, 75% e 60% da resistência) a uma relação R = 0,1. Com base nos resultados foram propostos coeficientes de redução de resistência à fadiga da emenda dentada em relação à madeira maciça e verificar que não há variação significativa da rigidez em função do número de ciclos.
Título en inglés
not available
Palabras clave en inglés
Fatigue
Finger joints
Glulam
Resumen en inglés
The aims of this work is the study of the fatigue strength and stiffness of the finger joints in tension, in order to propose an experimental methodology and to determine a strength reduction coefficient, in relation to solid wood, contributing to the characterization of these joints. Two wood species, Pinus caribea hondurensis and Eucalyptus grandis, and two adhesives types were used, being an industrial one phenol-resorcinol based and a poliuretane castor oil resin based, developed at the lnstitute of Chemistry of São Carlos. Cyclical tests were accomplished in three frequency levels (1 Hz, 5 Hz and 9 Hz) and three tension levels (90%, 75% and 60% of the strength) to a relationship R = 0,1. Based on the results, it were proposed strength reduction coefficients in relation to solid wood, for finger joints under fatigue in tension, and to concluded that there is no significant variation in stiffness with the cycle numbers.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-05-18
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.