Dissertação de Mestrado
DOI
10.11606/D.18.2016.tde-02022016-090733
Documento
Autor
Nome completo
Aldo Braghini Junior
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 1998
Orientador
Banca examinadora
Coelho, Reginaldo Teixeira (Presidente)
Diniz, Anselmo Eduardo
Oliveira, João Fernando Gomes de
Título em português
Investigação do desgaste de ferramentas de PCBN e metal duro no fresamento de topo de aços endurecidos
Palavras-chave em português
Fresamento de topo
Metal duro
Metal endurecido
PCBN
Resumo em português
O fresamento de topo de aços ferramenta, no estado endurecido, pode ser uma alternativa para a fabricação de moldes e matrizes, com alta taxa de remoção. Este trabalho estuda os tipos e mecanismos de desgaste presentes nesta operação de usinagem, bem como o comportamento da emissão acústica. São realizados experimentos com ferramentas de PCBN e Metal Duro usinando os aços H13 (49-51 HRc), VMO (54-57 HRc) e VC131 (57-59 HRc). O desgaste das ferramentas de PCBN é significativamente menor que o desgaste das ferramentas de Metal Duro. O tipo de desgaste predominante é o desgaste de flanco, com indícios de desgastes de cratera. É observada uma combinação entre os mecanismos de desgaste abrasivo e adesivo. Não se observa a formação de trincas abaixo da superfície usinada. Verifica-se que a emissão acústica aumenta com a velocidade de corte e mostra-se também dependente do material da peça e da ferramenta.
Título em inglês
not available
Palavras-chave em inglês
Carbide
Endmilling
Hardened material
PCBN
Resumo em inglês
The endmilling operation applied to the machining of hardened tool steels, can be seen as an alternative to the conventional sequence of operations used in dies and injection moulds. Normally, eletrodischarge machining, which has a low removal rate, is applied for the finishing operation, just before polishing. The present research work study the types and mechanisms of wear that appear in this machining operation, as well as, the behaviour of Acoustic Emission (EA). Experiments are carried out using PCBN and Carbide tools, machining AISI H13 (49-51 HRc), AISI 6F3 (54-57 HRc) e AISI D6 (57-59 HRc). The wear observed on the PCBN tools was smaller than that on the carbide ones. The type of wear dominating was flank wear, with some presence of crater wear in a few machining conditions. It was also observed a combination between the abrasive and the adhesive mechanisms. It was not noted any cracks on the surface just below the machined surface. The acoustic emission showed to be directly proportional to the cutting speed and also dependent upon the workpiece material and to the tool material.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2016-02-02
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.