Disertación de Maestría
DOI
10.11606/D.18.2016.tde-15032016-134826
Documento
Autor
Nombre completo
Tadeu Tomio Sudo
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2001
Director
Tribunal
Coelho, Reginaldo Teixeira (Presidente)
Ruffino, Rosalvo Tiago
Schützer, Klaus
Título en portugués
Uma contribuição ao estudo do torneamento com alta velocidade
Palabras clave en portugués
Cerâmica
Ferro fundido cinzento
GG25
Metal duro
MQL
Torneamento com alta velocidade
Usinagem a seco
Usinagem com alta velocidade
Resumen en portugués
O material, metálico ferro fundido cinzento, é muito utilizado industrialmente, principalmente na área automobilística. Usinagem com alta velocidade tem sido uma tendência atual para aumentar a produtividade, com a possibilidade de se ober ótima qualidade superficial, possivelmente eliminando processos subseqüentes. Aliado à questão de qualidade ambiental, as operações de usinagem têm-se voltado para usinagem a seco ou com mínima quantidade de lubrificante (MQL - minimal quantity of lubricant). Este trabalho estuda o torneamento com alta velocdidade de ferro fundido cinzento GG25 através de usinagem a seco e com MQL. Utiliza-se, em operação de faceamento, ferramenta de cerâmica mista (Al2O3+ TiC) e metal duro com cobertura (TiCN/Al2O3/TiN), usando velocidades de corte muito acima dos valores tradicionais. Comparativamente o desgaste é significativamente menor na cerâmica. O tipo de desgaste predominante é o desgaste de flanco. Os principais mecanismos de desgaste encontrados são abrasão mecânica e delaminação. O aumento do avanço diminui o desgaste de flanco. Existe uma razão entre a vazão de óleo e a vazão de ar na lubrificação MQL que viabiliza sua aplicacão com relação ao desgaste de flanco. Em todas as condições testadas, o sistema MQL mostra ser capaz de reduzir a rugosidade superficial Ra.
Título en inglés
A contribution to the study of high speed turning
Palabras clave en inglés
Carbide
Ceramic
Dry machining
GG25
Gray cast iron
High speed machining
High speed turning
MQL
Resumen en inglés
The gray cast iron material is very used industrially, mainly in the automotive industry. High speed machining is the current tendency to increase the productivity, with the possibility of obtaining good surface quality, possibly eliminating subsequent operations. Due to regulations on the subject of environrnental quality, the machining operations have been turned to dry machining or minimal quantity of lubricant (MQL). This work studies the turning process at high speed of gray cast iron GG25 with dry machining and MQL techniques. The operation uses face turning with coated carbide (TiCN/Al2O3/TiN) and mixed alumina ceramic (Al203+ TiC) with cutting speeds much higher than the traditional recommended values. Comparatively, the wear is significantly smaller in the mixed alumina ceramic tools. The predominant type of wear is the flank wear. The main wear mechanisms are mechanical abrasion and delamination. The increase of feed values shows some reduction on the flank wear. It seems to exist an ideal ratio of oil to air in the MQL system, which makes possible its application for reducing flank wear on the tools. In all conditions tested, the MQL system shows to be able to reduce surface roughness (Ra).
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-03-15
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.