Thèse de Doctorat
DOI
10.11606/T.18.2017.tde-03102017-142025
Document
Auteur
Nom complet
Neide Aparecida Mariano
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1997
Directeur
Jury
Spinelli, Dirceu (Président)
Bose Filho, Waldek Wladimir
Ferreira, Itamar
Gomes, Samuel Irati Novaes
Kuri, Sebastião Elias
Titre en portugais
Corrosão sob tensão de um aço inoxidável austenítico em soluções aquosas contendo cloretos
Mots-clés en portugais
Aço inoxidável
Cloretos
Corrosão sob tensão
Fator limite de intensidade de tensão
Resumé en portugais
No presente trabalho foi estudado o comportamento de um aço inoxidável austenítico do sistema Fe-Cr-Mn-N, nas condições como recebido, solubilizado e sensitizado, quando submetidos à meios contendo cloretos. Para analisar a suscetibilidade à corrosão sob tensão foram utilizados corpos de prova dos tipos DCB ("Double Cantilever Beam") e C(T) ("Compact- Tension"), pré-trincados em fadiga, com entalhes laterais e carregados com cunhas. Os meios empregados foram as soluções aquosas 45% em peso de MgCl2 na temperatura de ebulição de 154°C, água do mar sintética na temperatura ambiente e de ebulição de 100°C e 3,5% em peso de NaCI na temperatura ambiente. A suscetibilidade à corrosão sob tensão foi avaliada em termos do fator limite de intensidade de tensão, KISCC, e foram caracterizados os aspectos fractográficos dos corpos de prova em que ocorreram propagação de trinca por corrosão sob tensão. Foi verificado que apenas os corpos de prova do aço E3949 nas condições como recebido e sensitizado, foram suscetíveis à corrosão sob tensão em solução aquosa de 45% em peso de MgCl2 na temperatura de ebulição. Também foi determinado o comportamento eletroquímico do material nas condições citadas acima com relação aos meios empregados. Os resultados das curvas de polarização obtidas mostraram que o material apresenta baixa resistência à corrosão, principalmente em meios de MgCl2.
Titre en anglais
Stress corrosion cracking of austenitic stainless steel in chlorides environments
Mots-clés en anglais
Austenitic stainless steel
Chloride
Stress corrosion cracking
Threshold stress intensity factor
Resumé en anglais
The present work studies the stress corrosion cracking behavior in austenitic Fe-Cr-Mn-N stainless steel, in as received, solubilized and sensitized conditions, when submited to several chlorides environments. To evalued the stress corrosion cracking susceptibility, DCB ("Double Cantilcver Beam") and C(T) ("Compact- Tension") specimens, fatigue precracked, side grooved and wedge loaded were used. The environments employed were boiling solution of 45 wt% of MgCl2 at 154ºC, synthetic sea water at room and 100°C temperatures, and a solution with 3,5 wt% of NaCI at room temperature. The susceptibility to stress corrosion cracking has been evaluated in terms of the threshold stress intensity factor, KISCC, and the fracture surface appearance of those specimens whose the crack propagation took place was characterized. The results showed that only the specimens in the as received and sensitized conditions, were suceptible to the stress corrosion cracking effect in the solution with 45 wt% of MgCl2 at the boilling temperature. Also, it has been verified the electrochemical behavior of this steel when submited in the above environments. The results of polarization curves showed that the material presents low corrosion strength, mainly in MgCl2 environments.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2017-10-03
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.