• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Tesis Doctoral
DOI
10.11606/T.18.2017.tde-09102017-115927
Documento
Autor
Nombre completo
Luiz Vicente Vareda
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1997
Director
Tribunal
Spinelli, Dirceu (Presidente)
Bose Filho, Waldek Wladimir
Conceição, Ideonor Novaes da
Fernandes, Odilson Coimbra
Ferreira, Itamar
Título en portugués
Avaliação das propriedades mecânicas de fadiga de baixo e alto ciclo e tenacidade à fratura de um aço inoxidável austenítico do sistema Cr-Mn-N
Palabras clave en portugués
Aço inoxidável austenítico
Fadiga de alto ciclo
Fadiga de baixo ciclo
Tenacidade à fratura
Resumen en portugués
Neste trabalho, foram determinadas as propriedades mecânicas de fadiga de baixo e alto ciclo e de tenacidade à fratura JIC de um aço inoxidável austenítico do sistema Cr-Mn-N, utilizado na confecção de colares para perfurações pela indústria de exploração de petróleo. Foi também avaliada a influência da temperatura de serviço nas propriedades mecânicas do aço, que apresentou um decréscimo significativo nos valores dos limites de escoamento e de resistência e do alongamento com o aumento da temperatura. Na temperatura ambiente, os ensaios de fadiga de baixo e alto ciclo foram realizados segundo as normas ASTM E606 e ASTM E466. Em temperaturas superiores, as propriedades de fadiga foram estimadas utilizando alguns métodos atualmente disponíveis, que utilizam somente as propriedades mecânicas de tração. Os resultados obtidos mostraram uma pequena influência da temperatura na vida à fadiga na região de baixo ciclo e uma grande influência na região de alto ciclo. A curva tensão-deformação cíclica do material foi obtida pelo método convencional e pelo método do passo incrementai, que utiliza somente um corpo de prova. Os ensaios de JIC foram realizados nas temperaturas ambiente e 150°C, segundo a norma ASTM E813, utilizando a técnica de variação da flexibilidade elástica. Na temperatura ambiente, foi observada uma grande dispersão nos valores obtidos de JIC, atribuída à presença de uma fase frágil, identificada como precipitados de carbonitretos mistos de ferro, cromo, manganês e nióbio. Foi também observada uma diminuição no valor médio de JIC com o aumento da temperatura.
Título en inglés
Evaluation of the low and high cycle fatigue and fracture toughness mechanical properties of a Cr-Mn-N austenitic stainless steel
Palabras clave en inglés
Austenitic stainless steel
Fracture toughness
High cycle fatigue
Low cycle fatigue
Resumen en inglés
In the present work, the low and high cycle fatigue and fracture toughness properties of a Cr-Mn-N austenitic stainless steel used for application in drill collars were investigated. Also, the temperarure dependence of the tensile properties was determined, and it was found that the yield strength, ultimate strength and elongation values decrease significantly with the temperature. The low and high cycle fatigue testing were carried out at room temperature according to ASTM E606 and ASTM E466 standards. At high temperarure, the fatigue properties were estimated from monotonic propetties obtained in the tensile testing. The results showed small influence of temperature in the fatigue life in the short-life range and great influence in the long-life range. The cyclic stress-strain curve was obtained by companion specimen tests and incremental step tests methods. The last method showed to be advantageous because only one specimen and short testing time were required. The fracture toughness was detennined at room temperature and at 150°C applying elastic-plastic fracture mechanics concepts. The single specimen elastic compliance technique for crack length determination was employied. At room temperature a great scattering of the JIC values was observed due the presence of the brittle phase identified as a precipitates of carbonitride content Fe, Cr, Mn, Nb elements. Also a decreasing of average value o f the JIC was observed with the increasing of temperature.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Tese_Vareda_LuizV.pdf (50.11 Mbytes)
Fecha de Publicación
2017-10-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.