Disertación de Maestría
DOI
10.11606/D.18.2017.tde-09102017-163044
Documento
Autor
Nombre completo
Isabel Cristina Buttignon
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1995
Director
Tribunal
Rollo, João Manuel Domingos de Almeida (Presidente)
Canale, Lauralice de Campos Franceschini
Zavaglia, Cecília Amélia de Carvalho
Título en portugués
Berílio, elemento envelhecedor dos aços inoxidáveis austeníticos
Palabras clave en portugués
Aços inoxidáveis austeníticos
Berílio
Resumen en portugués
Foi estudado o efeito do elemento químico berílio nos aços inoxidáveis austeníticos objetivando um material com boas propriedades mecânicas e resistência à corrosão. Para isso foram fundidas a vácuo, três ligas inoxidáveis experimentais utilizando a matriz do aço inoxidável austenítico AISI do tipo 18-10. Os resultados foram direcionados às ligas experimentais nos estados solubilizado; solubilizado e envelhecido; solubilizado deformado 30% e envelhecido. Os testes metalográficos, de microdureza, corrosão e dilatométricos evidenciaram o berílio como um elemento de forte efeito envelhecedor, em tempos de tratamento relativamente curtos, propiciando aos aços inoxidáveis experimentais bons padrões de alongamento em parceria com boa resistência ao escoamento. Tais parâmetros possibilitam às ligas experimentais serem utilizadas como materiais que possam ser obtidos em formas desejadas e possuindo a propriedade que não é própria dos aços inoxidáveis austeníticos, isto é, o envelhecimento.
Título en inglés
not available
Palabras clave en inglés
not available
Resumen en inglés
The effect of the chemical element beryllium in austenitic stainless steel was studied as an attempt to design a material with good mechanical properties and resistent to corrosion. Three experimental stainless steel alloy were cast in vaccum using the matrix of the austenitic stainless steel type 18-10. The results were directed with the experimental alloys in the states solubilised, solubilised and aged, and solubilised and worked to 30% and aged. The metallographic, micro-hardness, corrosion and dilatometric tests showed the remarkable effect of the element beryllium as a powerful aging agent for relatively short treatment times giving good paters of elongation as well as good mechanical properties to the tested stainless steels. Such parameters make it possible for the experimental alloys, to be used as materiais in different shapes and having the property which is not a characteristic of this steel, that is, aging.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-10-09
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.