Master's Dissertation
DOI
10.11606/D.18.1997.tde-17012011-161430
Document
Author
Full name
César Augusto de Jesus Falcão
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 1997
Supervisor
Committee
Spinelli, Dirceu (President)
Gomes, Samuel Irati Novaes
Kiminami, Cláudio Shyinti
Title in Portuguese
Avaliação da tenacidade à fratura na zona termicamente afetada de soldas múltiplos passes em um aço ARBL
Keywords in Portuguese
Aço alta resistência e baixa liga
CTOD
Tenacidade à fratura
Zona termicamente afetada
Abstract in Portuguese
O presente trabalho avalia e compara os resultados da tenacidade à fratura da zona termicamente afetada (ZTA) de soldas múltiplos passes por meio de ensaios de CTOD. Para este estudo, foi utilizado um aço alta resistência e baixa liga (ARBL) resistente à corrosão ambiental. As soldas foram realizadas com insumo de calor de 30 e 50 kJ/cm em um chanfro 1/2 K. Os resultados dos ensaios de CTOD mostraram que a solda produzida com maior insumo de calor apresenta tenacidade à fratura mais elevada. A análise microestrutural revelou que as microestruturas de elevada dureza e baixa tenacidade, formadas na ZTA de granulação grosseira, para a condição de 30 kJ/cm, deram lugar às microestruturas de tenacidade mais elevada, para o insumo de calor de 50 kJ/cm.
Title in English
Evaluation of fracture toughness in heat affected zone of multiple pass welds in a high strength low alloy steel
Keywords in English
CTOD
Fracture toughness
Heat affected zone
High strength low alloy steel
Abstract in English
In this work the fracture toughness results of the heat affected zone (HAZ) in a multiple pass welds using a crack tip opening displacement (CTOD) concept were evaluated and compared. It was used an ambiental resistent high strengh low alloy steel. The welds were carried out using a heat input of 30 and 50 kJ/cm in a bevel preparation 1/2 K. The results of CTOD testing showed that increasing heat input, caused an improvement in the weldments fracture toughness. Microstructural analysis revealed that the high hardness and low toughness microstructures formed at coarse grain HAZ, near fusion line, for welding condition 30 kJ/cm were changed to higher toughness microstructure using a heat input of 50 kJ/cm.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2011-01-18
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.