Disertación de Maestría
DOI
10.11606/D.18.1997.tde-17012011-161430
Documento
Autor
Nombre completo
César Augusto de Jesus Falcão
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 1997
Director
Tribunal
Spinelli, Dirceu (Presidente)
Gomes, Samuel Irati Novaes
Kiminami, Cláudio Shyinti
Título en portugués
Avaliação da tenacidade à fratura na zona termicamente afetada de soldas múltiplos passes em um aço ARBL
Palabras clave en portugués
Aço alta resistência e baixa liga
CTOD
Tenacidade à fratura
Zona termicamente afetada
Resumen en portugués
O presente trabalho avalia e compara os resultados da tenacidade à fratura da zona termicamente afetada (ZTA) de soldas múltiplos passes por meio de ensaios de CTOD. Para este estudo, foi utilizado um aço alta resistência e baixa liga (ARBL) resistente à corrosão ambiental. As soldas foram realizadas com insumo de calor de 30 e 50 kJ/cm em um chanfro 1/2 K. Os resultados dos ensaios de CTOD mostraram que a solda produzida com maior insumo de calor apresenta tenacidade à fratura mais elevada. A análise microestrutural revelou que as microestruturas de elevada dureza e baixa tenacidade, formadas na ZTA de granulação grosseira, para a condição de 30 kJ/cm, deram lugar às microestruturas de tenacidade mais elevada, para o insumo de calor de 50 kJ/cm.
Título en inglés
Evaluation of fracture toughness in heat affected zone of multiple pass welds in a high strength low alloy steel
Palabras clave en inglés
CTOD
Fracture toughness
Heat affected zone
High strength low alloy steel
Resumen en inglés
In this work the fracture toughness results of the heat affected zone (HAZ) in a multiple pass welds using a crack tip opening displacement (CTOD) concept were evaluated and compared. It was used an ambiental resistent high strengh low alloy steel. The welds were carried out using a heat input of 30 and 50 kJ/cm in a bevel preparation 1/2 K. The results of CTOD testing showed that increasing heat input, caused an improvement in the weldments fracture toughness. Microstructural analysis revealed that the high hardness and low toughness microstructures formed at coarse grain HAZ, near fusion line, for welding condition 30 kJ/cm were changed to higher toughness microstructure using a heat input of 50 kJ/cm.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-01-18
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.