Mémoire de Maîtrise
DOI
10.11606/D.18.1997.tde-17012011-161430
Document
Auteur
Nom complet
César Augusto de Jesus Falcão
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 1997
Directeur
Jury
Spinelli, Dirceu (Président)
Gomes, Samuel Irati Novaes
Kiminami, Cláudio Shyinti
Titre en portugais
Avaliação da tenacidade à fratura na zona termicamente afetada de soldas múltiplos passes em um aço ARBL
Mots-clés en portugais
Aço alta resistência e baixa liga
CTOD
Tenacidade à fratura
Zona termicamente afetada
Resumé en portugais
O presente trabalho avalia e compara os resultados da tenacidade à fratura da zona termicamente afetada (ZTA) de soldas múltiplos passes por meio de ensaios de CTOD. Para este estudo, foi utilizado um aço alta resistência e baixa liga (ARBL) resistente à corrosão ambiental. As soldas foram realizadas com insumo de calor de 30 e 50 kJ/cm em um chanfro 1/2 K. Os resultados dos ensaios de CTOD mostraram que a solda produzida com maior insumo de calor apresenta tenacidade à fratura mais elevada. A análise microestrutural revelou que as microestruturas de elevada dureza e baixa tenacidade, formadas na ZTA de granulação grosseira, para a condição de 30 kJ/cm, deram lugar às microestruturas de tenacidade mais elevada, para o insumo de calor de 50 kJ/cm.
Titre en anglais
Evaluation of fracture toughness in heat affected zone of multiple pass welds in a high strength low alloy steel
Mots-clés en anglais
CTOD
Fracture toughness
Heat affected zone
High strength low alloy steel
Resumé en anglais
In this work the fracture toughness results of the heat affected zone (HAZ) in a multiple pass welds using a crack tip opening displacement (CTOD) concept were evaluated and compared. It was used an ambiental resistent high strengh low alloy steel. The welds were carried out using a heat input of 30 and 50 kJ/cm in a bevel preparation 1/2 K. The results of CTOD testing showed that increasing heat input, caused an improvement in the weldments fracture toughness. Microstructural analysis revealed that the high hardness and low toughness microstructures formed at coarse grain HAZ, near fusion line, for welding condition 30 kJ/cm were changed to higher toughness microstructure using a heat input of 50 kJ/cm.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2011-01-18
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.