• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
10.11606/D.18.2013.tde-17102013-100748
Documento
Autor
Nombre completo
André Anitelli
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2013
Director
Tribunal
Furlan, Ana Paula (Presidente)
Fabbri, Glauco Tulio Pessa
Takeda, Marcelo de Castro
Título en portugués
Estudo do dano por umidade de misturas densas com ligantes asfálticos convencional e modificado com polímero SBS
Palabras clave en portugués
Asfaltos convencionais e modificados com polímeros
Envelhecimento em curto e em longo prazo
Misturas asfálticas densas
Propriedades mecânicas
Suscetibilidade ao dano por umidade
Resumen en portugués
O objetivo desta pesquisa foi contribuir para o entendimento sobre a suscetibilidade ao dano por umidade de misturas asfálticas densas à luz dos ensaios da ASTM D 4867 e AASHTO T 283. Para isso, foi desenvolvido um programa experimental completo que considerou a variação, em dois níveis, dos seguintes fatores: tipo de asfalto (CAP 50/70 e CAP 50/70+SBS), presença de aditivo (sem e com cal) e modo de preparo (envelhecimentos em curto e em longo prazos). O programa experimental resultou em 8 tipos de misturas asfálticas (condições experimentais) que foram caracterizadas em suas propriedades originais e após um condicionamento térmico composto de uma fase de congelamento (-18º C por 16 horas) e uma fase de descongelamento (60º C por 24 horas). A partir das análises dos resultados foi possível constatar que (i) nenhuma mistura testada foi considerada suscetível ao dano por umidade, mas a relação de resistência à tração das misturas com CAP 50/70 de ambos os métodos se encontraram no limiar dos valores limites; (ii) as misturas com asfalto modificado, em geral, apresentaram maiores valores de módulo de resiliência e resistência à tração e foram mais resistentes à ação da água; (iii) a adição de cal não promoveu mudanças notáveis nas propriedades originais, no entanto contribuiu para a manutenção ou para o aumento da resistência ao dano por umidade; (iv) os envelhecimentos em curto e longo prazos dos métodos da ASTM e da AASHTO não provocaram mudanças importantes nas propriedades originais e após o condicionamento as misturas testadas exibiram tendências de comportamentos similares.
Título en inglés
Study of moisture damage of conventional and polymer modified asphalt mixtures
Palabras clave en inglés
Conventional and polymer modified asphalts
Hot mixture asphalt
Mechanical properties
Moisture damage susceptibility
Short and long term aging
Resumen en inglés
This research presents a contribution to understanding hot mix asphalt (HMA) moisture damage susceptibility according to ASTM D 4867 and AASHTO T 283 tests. A full factorial experiment design was carried out considering the factor variations, on two levels: asphalt type (CAP 50/70 and CAP 50/70+SBS), additive presence (with or without hydrated lime) and mixture procedure (short and long term aging). The experimental program resulted in 8 types of asphalt mixes (experimental conditions) which were characterized by the original properties and after a thermal conditioning wich consisted of a freezing phase (-18 °C for 16 hours) and a thawing phase (60 °C for 24 hours). Findings indicate that (i) no one mix was considered susceptible to moisture damage, however the ITR (indirect tensile ratio) of the CAP 50/70 mixes resulted ITR near to protocol admissible values; (ii) in general, CAP 50/70+SBS mixes presented higher resilient modulus, indirect tensile strength and indirect tensile ratio values, (iii) the addition of hydrated lime did not show remarkable changes in original properties, nevertheless it contributed for maintaining or increasing the moisture damage resistance; (iv) short and long term aging procedures (ASTM and AASHTO) did not cause important changes in original properties and after conditioning the mixes showed similar behavior tendencies.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
AndreAnitelli.pdf (1.93 Mbytes)
Fecha de Publicación
2013-10-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.