Mémoire de Maîtrise
DOI
10.11606/D.18.2013.tde-17102013-100748
Document
Auteur
Nom complet
André Anitelli
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2013
Directeur
Jury
Furlan, Ana Paula (Président)
Fabbri, Glauco Tulio Pessa
Takeda, Marcelo de Castro
Titre en portugais
Estudo do dano por umidade de misturas densas com ligantes asfálticos convencional e modificado com polímero SBS
Mots-clés en portugais
Asfaltos convencionais e modificados com polímeros
Envelhecimento em curto e em longo prazo
Misturas asfálticas densas
Propriedades mecânicas
Suscetibilidade ao dano por umidade
Resumé en portugais
O objetivo desta pesquisa foi contribuir para o entendimento sobre a suscetibilidade ao dano por umidade de misturas asfálticas densas à luz dos ensaios da ASTM D 4867 e AASHTO T 283. Para isso, foi desenvolvido um programa experimental completo que considerou a variação, em dois níveis, dos seguintes fatores: tipo de asfalto (CAP 50/70 e CAP 50/70+SBS), presença de aditivo (sem e com cal) e modo de preparo (envelhecimentos em curto e em longo prazos). O programa experimental resultou em 8 tipos de misturas asfálticas (condições experimentais) que foram caracterizadas em suas propriedades originais e após um condicionamento térmico composto de uma fase de congelamento (-18º C por 16 horas) e uma fase de descongelamento (60º C por 24 horas). A partir das análises dos resultados foi possível constatar que (i) nenhuma mistura testada foi considerada suscetível ao dano por umidade, mas a relação de resistência à tração das misturas com CAP 50/70 de ambos os métodos se encontraram no limiar dos valores limites; (ii) as misturas com asfalto modificado, em geral, apresentaram maiores valores de módulo de resiliência e resistência à tração e foram mais resistentes à ação da água; (iii) a adição de cal não promoveu mudanças notáveis nas propriedades originais, no entanto contribuiu para a manutenção ou para o aumento da resistência ao dano por umidade; (iv) os envelhecimentos em curto e longo prazos dos métodos da ASTM e da AASHTO não provocaram mudanças importantes nas propriedades originais e após o condicionamento as misturas testadas exibiram tendências de comportamentos similares.
Titre en anglais
Study of moisture damage of conventional and polymer modified asphalt mixtures
Mots-clés en anglais
Conventional and polymer modified asphalts
Hot mixture asphalt
Mechanical properties
Moisture damage susceptibility
Short and long term aging
Resumé en anglais
This research presents a contribution to understanding hot mix asphalt (HMA) moisture damage susceptibility according to ASTM D 4867 and AASHTO T 283 tests. A full factorial experiment design was carried out considering the factor variations, on two levels: asphalt type (CAP 50/70 and CAP 50/70+SBS), additive presence (with or without hydrated lime) and mixture procedure (short and long term aging). The experimental program resulted in 8 types of asphalt mixes (experimental conditions) which were characterized by the original properties and after a thermal conditioning wich consisted of a freezing phase (-18 °C for 16 hours) and a thawing phase (60 °C for 24 hours). Findings indicate that (i) no one mix was considered susceptible to moisture damage, however the ITR (indirect tensile ratio) of the CAP 50/70 mixes resulted ITR near to protocol admissible values; (ii) in general, CAP 50/70+SBS mixes presented higher resilient modulus, indirect tensile strength and indirect tensile ratio values, (iii) the addition of hydrated lime did not show remarkable changes in original properties, nevertheless it contributed for maintaining or increasing the moisture damage resistance; (iv) short and long term aging procedures (ASTM and AASHTO) did not cause important changes in original properties and after conditioning the mixes showed similar behavior tendencies.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
AndreAnitelli.pdf (1.93 Mbytes)
Date de Publication
2013-10-21
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.