Tesis Doctoral
DOI
10.11606/T.18.2010.tde-17012011-160849
Documento
Autor
Nombre completo
Claudia Cristiane Camilo
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2010
Director
Tribunal
Fortulan, Carlos Alberto (Presidente)
Duailibi, Silvio Eduardo
Parizotto, Nivaldo Antonio
Purquerio, Benedito de Moraes
Zavaglia, Cecília Amélia de Carvalho
Título en portugués
Implantes de alumina em gradiente funcional de porosidade recobertos com hidroxiapatita e biovidro: avaliação da osseointegração
Palabras clave en portugués
Alumina
Cisalhamento interfacial
Histologia
Implante buco-maxilo-facial
Implante ósseo
Material com gradiente funcional
Resumen en portugués
Esta pesquisa tem como finalidade desenvolver implantes de alumina com núcleo denso e superfície gradualmente porosa (FGM) recobertos com materiais bioativos - hidroxiapatita e biovidro. Materiais porosos são estudados como solução para a osseointegração, porém apresenta déficit nas suas propriedades mecânicas. Estruturas bifásicas foram desenvolvidas por pesquisadores com o propósito de promover crescimento tecidual, sem afetar significativamente sua propriedade mecânica, no entanto ocorre delaminação. Neste trabalho é proposta uma estrutura em gradiente funcional que visa aprimorar as propriedades mecânicas conjugadas com a sinalização celular e com integração óssea. O tamanho, a morfologia de poros e também a porosidade são parâmetros fundamentais para boa resposta tecidual e integração do implante, pois afetam a viabilidade e a afinidade celular. Para essa finalidade a busca por uma espessura efetiva de porosidade se faz fundamental para alto desempenho do implante. Peças de alumina porosas infiltradas com materiais bioativos foram fabricadas e estudadas in vivo, em tíbias de ratos da raça Wistar durante 14, 18, 21 e 28 dias, para investigar a qualidade do crescimento de tecido ósseo. O estudo com implantes porosos recobertos foi realizado para avaliar e padronizar a superfície porosa do gradiente funcional. Os animais foram analisados com densidade mineral óssea (DMO), as tíbias foram caracterizadas na interface osso-implante e nos poros com histologia, com EDS-line-scan, com radiografias e com ensaios de cisalhamento. Implantes de alumina com 70% de porosidade foram comparados com recobrimento bioativo e sem recobrimento in vivo e ex-vivo. Nos resultados, os implantes recobertos aceleram o processo de osseointegração. Essa característica foi mais evidente no período de 28 dias de implantação com aumento de 24% na tensão de cisalhamento. Após validar uma superfície porosa e osseointegrável para a superfície do gradiente funcional, foram aplicadas técnicas diferenciadas para manufaturar peças com núcleo denso e superfície com gradiente de porosidade. As peças com FGM foram manufaturadas com a utilização de duas técnicas, dipping e co-prensagem e foram analisadas com microscopia eletrônica de varredura. Com o método de manufatura de co-prensagem foram obtidas peças com superfície gradualmente porosa, com transição de densificação contínua, sem delaminação. Os implantes de alumina em gradiente funcional com 70 % de porosidade na superfície mais externa, recobertos por bioativos apresentam potencial para aplicações em implantes ósseos ou dentários.
Título en inglés
Alumina implants with functional gradient of porosity coated with hydroxyapatite and bioactive glass: evaluation of osseointegration
Palabras clave en inglés
Alumina
Bone implants
Buccomaxillo-facial implants
Functional gradient materials
Push-out tests
Resumen en inglés
The present thesis reports on the development of alumina implants with dense core and gradually porous surface (FGM) covered with bioactive materials, hydroxyapatite (HA) and bioactive glass. Porous materials have been studied to provide tissue ingrowth, however they strongly affect the mechanical properties of the implant. Biphasic structures have been developed by some researchers to promote tissue growth without affecting the mechanical properties, although delamination may occur. This study proposes a functional gradient structure to improve both the mechanical properties of the material and cell signaling. The size and morphology of the pores as well as their porosity are key parameters for good tissue response and implant integration, since they affect the viability and cell affinity, and an effective porosity thickness becomes essential for a high performance of the implant. Porous alumina implants coated with bioactive materials were fabricated and studied in vivo in rat tibia for 14, 18, 21, and 28 days to investigate the quality of bone tissue growth. The study of porous coated implants was performed to evaluate and standardize the porous surface of the functional gradient. The animals were examined with bone mineral density (BMD), the tibiae were characterized in the bone-implant interface and the pores were analyzed with histology, EDS line-scan, X-ray and shear tests. Alumina with 70% porosity was compared with and without bioactive coating in vivo and ex vivo. The results showed that the covered implants accelerated the osseointegration process. This characteristic is more evident within 28 days of deployment with a 24% increase in shear stress. After validating a porous and osteointegrated surface for the surface of the functional gradient, several techniques were applied to manufacture parts with dense core and surface with gradient of porosity. The pieces were manufactured with FGM using two techniques, dipping and co-pressing and were analyzed by scanning electron microscopy. The manufacturing method of co-pressing allowed obtaining pieces with gradually porous surface and continuous transition of densification without delamination. On the outermost surface, alumina implants with functional gradient and 70% porosity and coated with bioactive materials presented potential for application to bone or dental implants.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2011-02-22
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2021. Todos los derechos reservados.