Master's Dissertation
DOI
10.11606/D.18.2009.tde-13012011-150331
Document
Author
Full name
Cleber Michel Chiqueti
Institute/School/College
Knowledge Area
Date of Defense
Published
São Carlos, 2009
Supervisor
Committee
Canale, Lauralice de Campos Franceschini (President)
Muñoz Riofano, Rosamel Melita
Ruchert, Cassius Olivio Figueiredo Terra
Title in Portuguese
Estudo das distorções em aços AISI 5160 e AISI 6150 com variação da temperatura e da agitação do meio de resfriamento
Keywords in Portuguese
Deformação
Distorções em têmpera
Meios de resfriamento
Tensão residual
Tratamento térmico
Abstract in Portuguese
A distorção em tratamento térmico é a maior causa dos problemas na indústria. Existem vários parâmetros que compõem esse fenômeno. Com o avanço da tecnologia, a medição de algumas variáveis intrínsecas ao fenômeno da distorção se tornou possível, auxiliando no melhor conhecimento do processo o que resulta na diminuição do retrabalho e sucata na indústria. A concretização de melhoria em processos produtivos já é uma realidade; que se tornou possível com a diminuição dos limites de padronização e com processos de produção bem definidos e simplificados. Estudos localizados em determinados produtos específicos, bem como os seus meios de resfriamentos estão em constante evolução, tornando possível a troca de informação e tecnologia, auxiliando na diminuição dos desperdícios e contribuindo para a mitigação dos impactos ambientais. Esse trabalho visa estudar as distorções produzidas em aços AISI 5160 e AISI 6150, com corpos de prova sensíveis a distorção, variando alguns fatores como, mudança em três níveis de temperatura e em três níveis de agitação em óleo mineral convencional; os quais fazem parte do processo produtivo na indústria. Variando as temperaturas do meio de resfriamento e a agitação do banho, é possível determinar com o auxílio estatístico, metalográfico, das curvas de resfriamento e das curvas das taxas de resfriamento quais são as variáveis que tem influência na distorção. Esses resultados mostraram que a agitação e a temperatura do meio líquido de resfriamento são parâmetros imprescindíveis de controle para uma uniformidade da têmpera para a obtenção das características desejáveis.
Title in English
Distortion studies in AISI 5160 and AISI 6150 steel under variation of bath quenching temperature and agitation
Keywords in English
Deformation
Heat treatment
Quenchant
Quenching distortion
Residual stress
Abstract in English
The heat treatment distortion is the biggest cause of problems at companies. There are many parameters which cause this phenomenon. Studies in specific products, as well as in the quenchants are always progressing what became possible the dissemination of information and also the technology, helping to decreasing of waste and to improve environment. With the technology improvement, distortion phenomenon has become well known, resulting in better control of variables decreasing scrap metal and rework. However, this subject still needs to be investigated. In his context, this work studies the distortion phenomenon in two different steels (AISI 5160 and AISI 6150) under variable conditions of the cooling. Mineral oil quenchant in three bath temperatures and three agitation levels were used in this work. Changing those parameters it was possible to determinate which conditions would promote worst results in terms of distortion. Statistics studies, cooling curves analysis and metallographic observation offered support for the obtained conclusion.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
CleberChiqueti.pdf (1.73 Mbytes)
Publishing Date
2011-01-18
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2020. All rights reserved.