Disertación de Maestría
DOI
10.11606/D.18.2009.tde-13012011-160328
Documento
Autor
Nombre completo
Gladston Torres de Mesquita Alencar
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2009
Director
Tribunal
Casteletti, Luiz Carlos (Presidente)
Bolfarini, Claudemiro
Canale, Lauralice de Campos Franceschini
Título en portugués
Efeitos da adição de carbonetos na resistência ao desgaste e à corrosão de uma liga auto-fluxante depositada por aspersão térmica
Palabras clave en portugués
'B IND.4''C'
'SI''C'
Aspersão térmica
Auto-fluxantes ('NI''CR''B''SI''C')
Carbonetos
Corrosão
Desgaste
Resumen en portugués
Neste trabalho, visando-se melhorar o desempenho ao desgaste e/ou à corrosão de revestimentos de ligas auto-fluxantes, amostras de aço SAE 1020 foram revestidas pelo processo de aspersão térmica, sendo que uma delas foi revestida apenas com uma liga auto-fluxante a base de níquel ('NI"CR"B"SI"C') e outras duas, às quais aplicou-se essa liga com adições de carboneto de boro ou carboneto de silício. As camadas foram caracterizadas por meio de ensaios micrográficos ópticos e eletrônicos, microdurezas, corrosão e de microdesgaste. A camada adicionada com carboneto de boro apresentou o maior nível de dureza e melhor desempenho ao desgaste, seguida pela camada com carboneto de silício e a liga auto-fluxante pura. As amostras adicionadas de carboneto de boro e silício apresentaram comportamentos similares à corrosão, com potenciais de corrosão superiores ao da amostra sem adição.
Título en inglés
Effect of carbides addition in the wear and corrosion resistance of a sell-fluxing coating deposited by thermal spraying
Palabras clave en inglés
'B IND.4''C'
'SI''C'
Corrosion
Self-fluxings ('NI''CR''B''SI''C')
Thermal spraying
Wear
Resumen en inglés
In this work, aiming to improve the wear and/or corrosion performance of self-fluxing alloys coatings, samples SAE 1020 steel were coated by thermal spray process, one of then was coated only with a self-fluxing nickel-based ('NI"CR"B"SI"C') alloy and two others, in which was applied this alloy with additions of boron carbide or silicon carbide. The coatings were characterized by means of optical and electronic micrography, microhardness, corrosion and microwear tests. The coating added with boron carbide showed the highest level of hardness and the better wear performance, followed by the coating with silicon carbide and the pure self-fluxing alloy. The samples added with boron or silicon carbide showed similar corrosion performance, with higher corrosion potential in comparison to that presented by the sample without addition.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
TeseGladston.pdf (61.94 Mbytes)
Fecha de Publicación
2011-01-18
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.