Mémoire de Maîtrise
DOI
10.11606/D.18.2009.tde-13012011-160328
Document
Auteur
Nom complet
Gladston Torres de Mesquita Alencar
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2009
Directeur
Jury
Casteletti, Luiz Carlos (Président)
Bolfarini, Claudemiro
Canale, Lauralice de Campos Franceschini
Titre en portugais
Efeitos da adição de carbonetos na resistência ao desgaste e à corrosão de uma liga auto-fluxante depositada por aspersão térmica
Mots-clés en portugais
'B IND.4''C'
'SI''C'
Aspersão térmica
Auto-fluxantes ('NI''CR''B''SI''C')
Carbonetos
Corrosão
Desgaste
Resumé en portugais
Neste trabalho, visando-se melhorar o desempenho ao desgaste e/ou à corrosão de revestimentos de ligas auto-fluxantes, amostras de aço SAE 1020 foram revestidas pelo processo de aspersão térmica, sendo que uma delas foi revestida apenas com uma liga auto-fluxante a base de níquel ('NI"CR"B"SI"C') e outras duas, às quais aplicou-se essa liga com adições de carboneto de boro ou carboneto de silício. As camadas foram caracterizadas por meio de ensaios micrográficos ópticos e eletrônicos, microdurezas, corrosão e de microdesgaste. A camada adicionada com carboneto de boro apresentou o maior nível de dureza e melhor desempenho ao desgaste, seguida pela camada com carboneto de silício e a liga auto-fluxante pura. As amostras adicionadas de carboneto de boro e silício apresentaram comportamentos similares à corrosão, com potenciais de corrosão superiores ao da amostra sem adição.
Titre en anglais
Effect of carbides addition in the wear and corrosion resistance of a sell-fluxing coating deposited by thermal spraying
Mots-clés en anglais
'B IND.4''C'
'SI''C'
Corrosion
Self-fluxings ('NI''CR''B''SI''C')
Thermal spraying
Wear
Resumé en anglais
In this work, aiming to improve the wear and/or corrosion performance of self-fluxing alloys coatings, samples SAE 1020 steel were coated by thermal spray process, one of then was coated only with a self-fluxing nickel-based ('NI"CR"B"SI"C') alloy and two others, in which was applied this alloy with additions of boron carbide or silicon carbide. The coatings were characterized by means of optical and electronic micrography, microhardness, corrosion and microwear tests. The coating added with boron carbide showed the highest level of hardness and the better wear performance, followed by the coating with silicon carbide and the pure self-fluxing alloy. The samples added with boron or silicon carbide showed similar corrosion performance, with higher corrosion potential in comparison to that presented by the sample without addition.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
TeseGladston.pdf (61.94 Mbytes)
Date de Publication
2011-01-18
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.