Dissertação de Mestrado
DOI
10.11606/D.18.2009.tde-13012011-160328
Documento
Autor
Nome completo
Gladston Torres de Mesquita Alencar
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2009
Orientador
Banca examinadora
Casteletti, Luiz Carlos (Presidente)
Bolfarini, Claudemiro
Canale, Lauralice de Campos Franceschini
Título em português
Efeitos da adição de carbonetos na resistência ao desgaste e à corrosão de uma liga auto-fluxante depositada por aspersão térmica
Palavras-chave em português
'B IND.4''C'
'SI''C'
Aspersão térmica
Auto-fluxantes ('NI''CR''B''SI''C')
Carbonetos
Corrosão
Desgaste
Resumo em português
Neste trabalho, visando-se melhorar o desempenho ao desgaste e/ou à corrosão de revestimentos de ligas auto-fluxantes, amostras de aço SAE 1020 foram revestidas pelo processo de aspersão térmica, sendo que uma delas foi revestida apenas com uma liga auto-fluxante a base de níquel ('NI"CR"B"SI"C') e outras duas, às quais aplicou-se essa liga com adições de carboneto de boro ou carboneto de silício. As camadas foram caracterizadas por meio de ensaios micrográficos ópticos e eletrônicos, microdurezas, corrosão e de microdesgaste. A camada adicionada com carboneto de boro apresentou o maior nível de dureza e melhor desempenho ao desgaste, seguida pela camada com carboneto de silício e a liga auto-fluxante pura. As amostras adicionadas de carboneto de boro e silício apresentaram comportamentos similares à corrosão, com potenciais de corrosão superiores ao da amostra sem adição.
Título em inglês
Effect of carbides addition in the wear and corrosion resistance of a sell-fluxing coating deposited by thermal spraying
Palavras-chave em inglês
'B IND.4''C'
'SI''C'
Corrosion
Self-fluxings ('NI''CR''B''SI''C')
Thermal spraying
Wear
Resumo em inglês
In this work, aiming to improve the wear and/or corrosion performance of self-fluxing alloys coatings, samples SAE 1020 steel were coated by thermal spray process, one of then was coated only with a self-fluxing nickel-based ('NI"CR"B"SI"C') alloy and two others, in which was applied this alloy with additions of boron carbide or silicon carbide. The coatings were characterized by means of optical and electronic micrography, microhardness, corrosion and microwear tests. The coating added with boron carbide showed the highest level of hardness and the better wear performance, followed by the coating with silicon carbide and the pure self-fluxing alloy. The samples added with boron or silicon carbide showed similar corrosion performance, with higher corrosion potential in comparison to that presented by the sample without addition.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
TeseGladston.pdf (61.94 Mbytes)
Data de Publicação
2011-01-18
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2019. Todos os direitos reservados.