Mémoire de Maîtrise
DOI
10.11606/D.18.2008.tde-13062008-092505
Document
Auteur
Nom complet
Ramiro Carlos Guimarães
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2008
Directeur
Jury
Casteletti, Luiz Carlos (Président)
Bolfarini, Claudemiro
Canale, Lauralice de Campos Franceschini
Titre en portugais
Efeito da ferro-oxidação a vapor antes e após operação de usinagem na resistência ao desgaste de ferro sinterizado
Mots-clés en portugais
Desgaste
Ferro sinterizado
Tratamento a vapor
Usinagem
Resumé en portugais
Neste trabalho verificou-se o efeito da ferroxidação a vapor, aplicada antes e após operações de usinagem de acabamento final, na resistência ao desgaste de um ferro sinterizado, utilizado na fabricação de bielas usadas em mancais de deslizamento de compressor hermético. Ensaios micrográficos, de dureza e microdureza, ensaios de perfil e circularidade, testes de vida acelerados em um compressor hermético doméstico de refrigeração e ensaios de microdesgaste, usando-se o mesmo tipo de óleo aplicado em compressores, ou abrasivos com diferentes granulometrias, foram realizados em peças e amostras com e sem a camada ferroxidada. Verificou-se que a camada ferroxidada apresentou valores de durezas superiores ao do substrato em 130%. No caso das amostras ferroxidadas, os resultados indicaram significativa melhora na resistência ao desgaste tanto no teste de aplicação direta no compressor, demonstrado nos testes de perfis e de circularidades, como nos ensaios de microdesgaste, evidenciando a grande efetividade desse tratamento no aumento da resistência ao desgaste nas condições testadas neste trabalho.
Titre en anglais
Effect of steam treatment before and after machining operation on wear resistance of sintered steel
Mots-clés en anglais
Machining
Sintered steel
Steam treatment
Wear
Resumé en anglais
The intent of this work was to verify the effect of steam treatment applied before and after finishing machining operations on wear resistance of sintered steel used in the manufacturing of connecting rod applied in sliding bearings of hermetic compressor. Micrographic tests, hardness and micro hardness, test profile and roundness, accelerated endurance test in domestic refrigeration hermetic compressor and micro wear test using the same oil used in the compressor or abrasive with different grain size were made on parts and samples with and without oxide layer. It was verified that the oxide layer indicated hardness values over 130% than that of the substrate. In the case of layer oxide, the results showed significant improvement on wear resistance in the direct compressor application shown by test profile and roundness as well as micro wear test, showing the high efficiency of treatment increasing the wear resistance in the conditions tested in this work.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2008-06-30
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.