Disertación de Maestría
DOI
https://doi.org/10.11606/D.18.2017.tde-16112017-111032
Documento
Autor
Nombre completo
José Eduardo Nucci
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2014
Director
Tribunal
Canale, Lauralice de Campos Franceschini (Presidente)
Malafaia, Artur Mariano de Sousa
Vatavuk, Jan
Título en portugués
Comportamento ao impacto dos aços SAE 4140 e SAE 01 sob diferentes condições de tratamento térmico: temperado e revenido (com e sem banho criogênico) e austemperado
Palabras clave en portugués
Austêmpera
Criogênico
Têmpera e revenido
Resumen en portugués
Grandes partes dos estudos disponíveis na literatura sobre o comportamento dos materiais com microestruturas martensítica e bainítica relatam que a microestrutura bainítica, comparativamente à martensita revenida, promove melhores propriedades de impacto. No presente trabalho foi proposto o estudo de comportamento ao impacto de aços SAE 4140 e SAE 01 (VND) sob diferentes condições de tratamento térmico. Ao todo foram feitos 57 corpos de prova CHARPY para cada tipo de aço divididos em 3 lotes que foram então: temperados e revenidos, com e sem banho criogênico e austemperados. A dureza final após tratamento térmico foi similar nos diferentes tratamentos térmicos. Os resultados obtidos para os dois tipos de aço mostram que os corpos de provas que passaram pelo tratamento térmico de têmpera, revenido e banho criogênico apresentaram melhor tenacidade ao impacto.
Título en inglés
Behavior impact of SAE 4140 and SAE 01 steel under different conditions of heat treatment: quenched and tempered (with and without bath cryogenic) and austempered
Palabras clave en inglés
Austempering
Cryogenic process
Tempering and quenching
Resumen en inglés
Studies available in the literature about bainitic and martensitic microstructure report that bainitic microstructure compared to tempered martensite has better impact properties. In present work has proposed the study of the impact performance of steel SAE 4140 and SAE 01 (VND) under different conditions of heat treatment. A total 57 CHARPY specimens were divided in 3 sets, which were quenched and tempered, with and without cryogenic bath and austempered. The final hardness after heat treatment was similar in the different heat treatments. The results obtained for the two tipes of steel showed better impact performance for samples submitted to quenching tempering and cryogenie bath.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-11-16
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.