Dissertação de Mestrado
DOI
https://doi.org/10.11606/D.18.2017.tde-16112017-111032
Documento
Autor
Nome completo
José Eduardo Nucci
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2014
Orientador
Banca examinadora
Canale, Lauralice de Campos Franceschini (Presidente)
Malafaia, Artur Mariano de Sousa
Vatavuk, Jan
Título em português
Comportamento ao impacto dos aços SAE 4140 e SAE 01 sob diferentes condições de tratamento térmico: temperado e revenido (com e sem banho criogênico) e austemperado
Palavras-chave em português
Austêmpera
Criogênico
Têmpera e revenido
Resumo em português
Grandes partes dos estudos disponíveis na literatura sobre o comportamento dos materiais com microestruturas martensítica e bainítica relatam que a microestrutura bainítica, comparativamente à martensita revenida, promove melhores propriedades de impacto. No presente trabalho foi proposto o estudo de comportamento ao impacto de aços SAE 4140 e SAE 01 (VND) sob diferentes condições de tratamento térmico. Ao todo foram feitos 57 corpos de prova CHARPY para cada tipo de aço divididos em 3 lotes que foram então: temperados e revenidos, com e sem banho criogênico e austemperados. A dureza final após tratamento térmico foi similar nos diferentes tratamentos térmicos. Os resultados obtidos para os dois tipos de aço mostram que os corpos de provas que passaram pelo tratamento térmico de têmpera, revenido e banho criogênico apresentaram melhor tenacidade ao impacto.
Título em inglês
Behavior impact of SAE 4140 and SAE 01 steel under different conditions of heat treatment: quenched and tempered (with and without bath cryogenic) and austempered
Palavras-chave em inglês
Austempering
Cryogenic process
Tempering and quenching
Resumo em inglês
Studies available in the literature about bainitic and martensitic microstructure report that bainitic microstructure compared to tempered martensite has better impact properties. In present work has proposed the study of the impact performance of steel SAE 4140 and SAE 01 (VND) under different conditions of heat treatment. A total 57 CHARPY specimens were divided in 3 sets, which were quenched and tempered, with and without cryogenic bath and austempered. The final hardness after heat treatment was similar in the different heat treatments. The results obtained for the two tipes of steel showed better impact performance for samples submitted to quenching tempering and cryogenie bath.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2017-11-16
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2024. Todos os direitos reservados.