Mémoire de Maîtrise
DOI
10.11606/D.18.2012.tde-29082013-102825
Document
Auteur
Nom complet
Leticia Pereira Lira
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2012
Directeur
Jury
Casteletti, Luiz Carlos (Président)
Canale, Lauralice de Campos Franceschini
Picon, Carlos Alberto
Titre en portugais
Avaliação da resistência ao desgaste e à corrosão de revestimentos aspergidos termicamente em liga de alumínio AA 7475
Mots-clés en portugais
Aspersão térmica
Corrosão
Desgaste
Liga de alumínio AA 7475
Revestimentos
Resumé en portugais
Aspersão térmica é um processo de produção de revestimentos com ampla aplicação industrial, utilizado na proteção de superfícies contra a corrosão e/ou o desgaste. Os setores aeronáutico e de moldes plásticos estão entre os que utilizam essa técnica para ampliação da vida útil de seus componentes. Este trabalho teve como objetivo avaliar a influência do processo de deposição de revestimentos metálicos (1248 T - Co-28,5%Mo-17,5%Cr-3,4%Si e 1256 F - Co-28%Cr-4%W-3%Ni-3%Fe), cerâmicos (CRO 192 - Cr2O3-5%SiO2-3%TiO2 e 25030 - TiO2-8%Al2O3) e composto (1342 - WC-12%Co), aspergidos pelas técnicas de combustão por chama convencional (cerâmicos) e HVOF (metálicos e composto), no substrato constituído de uma liga de alumínio AA 7475 endurecida por precipitação, visando o melhoramento de suas características tribológicas (desgaste e corrosão), sem alterar as propriedades mecânicas. A influência do processo no substrato foi avaliada por meio de ensaios de microdureza Vickers, microestruturais e de composição química. A resistência ao desgaste foi avaliada por meio de ensaios de desgaste microabrasivo com esfera, com o uso de uma solução abrasiva de alumina (Al2O3). A avaliação da resistência à corrosão de revestimentos e substrato foi realizada por meio de ensaios de polarização potenciodinâmica em meio de NaCl 3,5%. A deposição dos revestimentos por aspersão térmica não afetou significativamente a dureza, composição química e microestrutura do substrato constituído pela liga de alumínio, tornando viável a aplicação dessa técnica a essa classe de ligas. Os revestimentos foram altamente eficientes na proteção do substrato contra o desgaste microabrasivo, sendo que o revestimento constituído de WC-Co (1342) apresentou o melhor desempenho dentre eles. Quanto à corrosão, todos os revestimentos apresentaram resistênciassuperiores a do substrato, tendo o revestimento Co-Cr-W-Fe-Ni (1256 F) apresentado o melhor desempenho geral. Portanto, os revestimentos produzidos por aspersão térmica são alternativas altamente promissoras para o melhoramento tribológico das ligas de alumínio envelhecidas, sem o comprometimento de suas características mecânicas.
Titre en anglais
Evaluation of wear resistance and corrosion resistance of thermally sprayed coatings of aluminum alloy AA 7475
Mots-clés en anglais
AA 7475 aluminum alloy
Coatings
Corrosion
Thermal spray
Wear
Resumé en anglais
The thermal spray process is used in the production of coatings with a wide range of industrial application such as protection of surfaces against corrosion and/or wear. The aircraft and plastic molds industries are among the ones that use this technique to increase the useful life of components. This work aimed to evaluate the influence of the deposition process of metallic (1248 T Co-28.5%Mo-17.5%Cr-3.4%Si and 1256 F Co-28%Cr-4%W-3%Ni- 3%Fe), ceramic (CRO 192 Cr2O3-5%SiO2-3%TiO2 and 25030 TiO2-8%Al2O3) and composite (1342 WC-12%Co) coatings, deposited by flame spray (for the ceramic) and HVOF (for the metallic and composite) techniques, on the substrate of precipitation-hardened AA 7475 aluminum alloy, intended to improve the tribological characteristics (wear and corrosion), without changing its mechanical properties. The influence of the process on the substrate was measured by Vickers microhardness, microstructural tests and chemical analyses. The wear resistance was evaluated by the calowear microabrasive test, using abrasive slurry of alumina (Al2O3). The corrosion resistance evaluation of coatings and substrate was carried out using the potentiodynamic polarization test in NaCl 3.5%. The coating deposition by thermal spray did not significantly affect the hardness, chemical composition and microstructure of the aluminum alloy substrate, establishing the feasibility of using this technique on this class of alloys. Coatings were highly efficient in protecting the substrate against microabrasive wear, where of the WC-Co (1342) coating showed the best performance among them. Also, the corrosion resistance of all coatings was higher than that of the substrate of which the Co-Cr-W-Fe-Ni (1256 F) coating presented the best overall performance. Therefore, the coatings produced by thermal spray are a highly promising alternative for the improvement of the tribological properties of aged aluminum alloys, without compromising its mechanical characteristics.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
LeticiaLira.pdf (6.97 Mbytes)
Date de Publication
2013-09-20
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.