Dissertação de Mestrado
DOI
10.11606/D.18.2016.tde-06052016-084651
Documento
Autor
Nome completo
João Paulo Sachetto
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Carlos, 2016
Orientador
Banca examinadora
Cavalheiro, Carla Cristina Schmitt (Presidente)
Bosquetti, Péricles
Sentanin, Franciani Cassia
Título em português
Efeito do tratamento térmico de STx-1b-Li+ na condutividade de filmes de STx-1b-Li+ /Alginato de sódio
Palavras-chave em português
Alginato de sódio
Argila
Tratamento térmico
Resumo em português
Neste trabalho foram estudados os efeitos causados pelo tratamento térmico na argila STx-1b-Li+ na condutividade de filmes argila/alginato de sódio. O argilomineral STx-1b foi submetido à substituição isomórfica do cátion Na+ por Li+ e posteriormente ao tratamento térmico em diferentes temperaturas. As argilas STx-1b-Li+ não tratada e tratada termicamente foram caracterizada por difração de raios-X (DRX) e termogravimetria (TG). As curvas TG mostraram que o argilomineral STx-1b-Li+ apresentou três perdas de massa que podem ser atribuídas à água adsorvida na argila, a água de hidratação dos íons Li+ e a água estrutural da argila. Para as argilas STx-1b-Li+ tratadas termicamente não foi observado a perda de massa associada à água quimicamente ligada aos contra-íons Li+. Estes resultados estão em concordância com os obtidos por DRX, onde observou-se uma diminuição no espaçamento interlamelar nas argilas tratadas termicamente. Em adição, foram preparados filmes de alginato de sódio com as argilas STx-1b-Li+ não tratada e tratada termicamente e estes foram caracterizados por calorimetria exploratória diferencia (DSC) e espectroscopia de impedância eletroquímica (EIE). As curvas DSC mostraram um aumento na temperatura de transição vítrea (Tg) dos filmes com o aumento da temperatura utilizada no tratamento das argilas. Este aumento nos valores de Tg é um indicativo que a mobilidade das cadeias diminuiu nos filmes polímero/argila que contém argilas tratadas em temperaturas mais elevadas. A espectroscopia de impedância eletroquímica (EIE) foi usada para avaliar-se a condutividade iônica dos filmes. Os resultados indicaram que os filmes contendo argilas que foram tratadas com temperaturas mais altas apresentaram menor condutividade.
Título em inglês
Effect of heat treatment of STx-1b-Li+ on the conductivity of STx-1b-Li+ /Sodium alginate films
Palavras-chave em inglês
Clay
Heat treatment
Sodium alginate
Resumo em inglês
In this work the effects caused by the heat treatment in STx-1b-Li+ clay on the conductivity of sodium alginate/clay were studied. The clay mineral STx-1b was submitted to isomorphous substitution of the Na+ for Li+ cation and subsequently to heat treatment at different temperatures. The STx-1b-Li+ clays untreated and heats treated were characterized by X-ray diffraction (XRD) and Thermogravimetric Analysis (TG). The TG curve showed that the clay mineral STL-1b-Li+ had three mass losses which can be attributed to adsorbed water in the clay, the water of hydration of the Li+ ions and structural clay water. To STx-1b-Li+ clays heat treated there were no mass loss associated to the water chemically bound to Li+ counter ions. These results are in agreement with those obtained by XRD, which it was observed a decrease in interlayer spacing in the heat treated clay. In addition, they were prepared sodium alginate films with STx-1b-Li+ clays untreated and heat treated and these films were characterized by Differential Scanning Calorimetry (DSC) and Electrochemical Impedance Spectroscopy (EIS). DSC curves showed an increase in glass transition temperature (Tg) of the films with temperature increasing used in the treatment of clays. This increase in Tg value is an indicative that the mobility of the chains had decrease in the polymer/clay films which contains heat treated clays at higher temperatures. The electrochemical impedance spectroscopy (EIS) was used to evaluate the ionic conductivity of the films. The results indicate that films containing clays which have been treated at higher temperatures had lower conductivity.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2016-05-11
 
AVISO: Saiba o que são os trabalhos decorrentes clicando aqui.
Todos os direitos da tese/dissertação são de seus autores
CeTI-SC/STI
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2021. Todos os direitos reservados.