Mémoire de Maîtrise
DOI
10.11606/D.18.2015.tde-11062015-171314
Document
Auteur
Nom complet
Willian Januário de Freitas
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2015
Directeur
Jury
Casteletti, Luiz Carlos (Président)
Balancin, Oscar
Bolfarini, Claudemiro
Titre en portugais
Influência da atmosfera de sinterização na dureza e resistência à corrosão do aço inoxidável 17-4 PH conformado a partir do processo de moldagem de pós por injeção
Mots-clés en portugais
Aço inoxidável 17-4 PH
Atmosferas de sinterização
Extração de ligantes primários e secundários
Moldagem de pós por injeção
Sinterização
Resumé en portugais
O processo de moldagem de pós injeção é utilizado para a fabricação de peças de geometrias complexas e com alto volume de produção. Em aplicações ortodônticas e médicas, nas quais são requeridas elevadas durezas e resistências à corrosão, o aço inoxidável 17-4 PH é utilizado aplicando-se aquela técnica de conformação. A atmosfera de sinterização é responsável pelo controle das reações químicas que ocorrem durante a densificação do material e são fundamentais para a qualidade final do produto. O objetivo deste trabalho foi avaliar a influência da atmosfera de sinterização na dureza e resistência à corrosão deste tipo de aço. A remoção dos ligantes primários foi realizada por meio de extração química utilizando-se um solvente com menor impacto ambiental, que se mostrou adequado a tal fim. A extração térmica posterior dos ligantes foi realizada pelo aquecimento nas temperaturas de 250°C e 450°C sendo, posteriormente, a temperatura elevada a 900°C, para o início da sinterização. Utilizou-se atmosferas de Nitrogênio, Vácuo e Hidrogênio, com temperaturas de sinterização de 1250°C e 1330°, com tempos de patamares de 30 e 60 minutos. Verificou-se que as densidades atingidas nas atmosferas de Hidrogênio e Vácuo são semelhantes e se adequaram às especificações requeridas pela norma, enquanto a atmosfera de Nitrogênio resultou em características inferiores. As durezas e as resistências à corrosão obtidas com o uso das atmosferas de Hidrogênio e Vácuo foram também superiores as das amostras sinterizadas em atmosfera de Nitrogênio.
Titre en anglais
Influence of sintering atmosphere in the hardness and corrosion resistance of 17-4 PH stainless steel shaped from powder injection molding process
Mots-clés en anglais
Metal injection molding
Primary and secondary binder removal
Sintering
Sintering atmospheres
Stainless steel 17-4 PH
Resumé en anglais
The powder injection molding process is used to manufacture parts with complex shapes, with high production demand. In orthodontic and medical applications, in which high hardness and corrosion resistance are required, 17-4 PH stainless steel is used by applying this forming technique. The sintering atmosphere is responsible for controlling the chemical reactions that occur during material densification and is critical to the ultimate product quality. This research study aims at evaluating the influence of the sintering atmosphere on the hardness and corrosion resistance of this type of steel. The removal of the primary binder was carried out by chemical extraction applying a solvent with less environmental impact, which has proved to be suitable for this purpose. The subsequent binder thermal extraction was held by heating at temperatures of 250°C and 450°C and, therefore, at temperature of 900°C, to initiate sintering. Nitrogen, vacuum and hydrogen atmospheres were used with sintering temperatures at 1250°C and 1330°, with 30 and 60 minute-step time. It was verified that the densities achieved in hydrogen and vacuum atmospheres are similar and suitable by the regulations, whereas the nitrogen atmosphere resulted in lower performance. The hardness and corrosion resistance obtained with the use of hydrogen and vacuum atmospheres were also higher than those obtained for samples sintered in the nitrogen atmosphere.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2015-06-17
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.