Mémoire de Maîtrise
DOI
https://doi.org/10.11606/D.18.2018.tde-12032018-103724
Document
Auteur
Nom complet
Mírian Akiko Kawamura
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2017
Directeur
Jury
Salomão, Rafael (Président)
Cabrelon, Marcelo Dezena
Oliveira, Ivone Regina de
Titre en portugais
Evolução microestrutural de cerâmicas porosas moldáveis à base de alumina e ligadas com cimento de aluminato de cálcio (CAC) e alumina hidratável (AH) durante aquecimento inicial até 1500°C
Mots-clés en portugais
Alumina hidratável
Cerâmica porosa
Cimento de aluminato de cálcio
Microestrutura
Refratário
Resumé en portugais
Cerâmicas porosas encontram um vasto campo de aplicações tecnológicas, tais como isolantes térmicos em equipamentos siderúrgicos, filtros de fluidos em altas temperaturas e biomateriais. A obtenção dessas estruturas por meio de moldagem direta de suspensões aquosas é uma interessante técnica de conformação, pois, peças com geometrias complexas e de grandes volumes podem ser produzidas. Neste caso, a consolidação ocorre, geralmente, pela ação de um ligante hidráulico, cuja função é garantir níveis mínimos de resistência mecânica à verde. Em sistemas refratários, os ligantes mais utilizados são o cimento de aluminato de cálcio (CAC) e alumina hidratável (AH), devido à alta refratariedade e custos competitivos destes materiais. Nas estruturas porosas à base de alumina, particularmente, eles podem proporcionar valores distintos de porosidade e diferentes tipos de microestruturas. Este trabalho teve como objetivo entender como o CAC e a AH interagem com a alumina. Foram avaliados a evolução microestrutural e os efeitos do teor (10 até 40% em volume de ligante hidráulico) e do tamanho das partículas da matriz (alumina fina e grossa) nas amostras à verde e durante o aquecimento inicial até 1500°C. De modo geral, maiores volumes de ligantes permitiram a obtenção de estruturas à verde mais rígidas e resistentes, porém menos porosas. Além da porosidade total (PT), as microestruturas decorrentes das transformações de fases cristalinas ou amorfas também influenciaram os resultados mecânicos. No caso do CAC, as fases formadas durante as reações in situ ajudaram a melhorar as propriedades mecânicas das amostras, mesmo que acompanhado por um acréscimo em porosidade. Em proporções estequiométricas, os cristais de hexaluminato de cálcio (CA6) formados após tratamento a 1500°C inibiram a densificação, ajudando na manutenção da PT (36,7-46,5%), ainda com boa resistência (acima de 20 MPa em compressão diametral). Nos sistemas ligados com AH, observou-se grandes perdas em propriedades mecânicas antes da sinterização, as quais foram relacionadas ao aumento de densidade real dos precipitados do ligante e à perda de conexão entre as partículas da matriz. Em altas temperaturas, os precipitados de AH auxiliaram a sinterização e garantiram a obtenção de peças porosas quando se utilizou alumina grossa (PT: 44,3-47,7%).
Titre en anglais
Microstructural evolution of porous castable ceramics based on alumina and binded by calcium aluminum cement (CAC) and hydratable alumina (HA) during initial heating up to 1500°C
Mots-clés en anglais
Calcium aluminate cement
Hydratable alumina
Microstructure
Porous ceramics
Refractory
Resumé en anglais
Porous ceramics have a wide range of technological applications, such as thermal insulation in steelmaking furnaces, filter for high temperature fluids and as biomaterials. Obtaining these structures through the direct casting of aqueous suspensions is an interesting conformation method since pieces with complex geometries and large volumes can be produced. In this case, the consolidation usually occurs by the action of a hydraulic binder, which provides the minimum levels of mechanical strength in green samples. In refractory systems, the most used binders are calcium aluminate cement (CAC) and hydratable alumina (HA), due to the high refractoriness and competitive costs of these materials. Particularly, in porous alumina-based structures, they can provide distinct values of porosity and different types of microstructures. The purpose of the present work is to understand how CAC and HA interact with alumina. The effects of the binder content (from 10 up to 40% in volume) and the particle size of the matrix (fine and coarse) during initial heating up to 1500°C were studied. In general, larger volumes of binders provided green samples with less porosity but higher mechanical strength. Besides total porosity (TP), the microstructures generated from the transformations of crystalline or amorphous phases also influenced the mechanical results. In the case of CAC, the phases formed by in situ reactions improved the mechanical properties of the samples, despite the increase in porosity. In stoichiometric proportions, the crystals of calcium hexaluminate (CA6) formed after treatment at 1500°C inhibited the densification, favoring to maintain total porosity (36.7-46.5%), even with acceptable mechanical properties (above 20 MPa under diametric compression). In HA-bonded systems, before the sintering begins, a decrease in mechanical properties was noted and related to the increase in density of the precipitates and loss of connection between the matrix particles. At high temperature, the precipitates from HA aided the sintering and guaranteed porous samples in coarse alumina composition (TP: 44.3- 47.7%).
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2018-03-19
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.