Disertación de Maestría
DOI
10.11606/D.18.2016.tde-12052016-092247
Documento
Autor
Nombre completo
Daniel Schuller
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2016
Director
Tribunal
Canale, Lauralice de Campos Franceschini (Presidente)
Campos, Valdemir Soares de
Voorwald, Herman Jacobus Cornelis
Título en portugués
Determinação da tenacidade à fratura do aço aeronáutico 300M, submetido a diferentes parâmetros de tratamentos térmicos e criogenia, utilizando técnica de corpo cilíndrico com entalhe
Palabras clave en portugués
Aço 300M
Aço Aeronáutico
Corpo cilíndrico entalhado
Tenacidade à Fratura
Resumen en portugués
Foi realizado estudo sobre a influência da variação de alguns parâmetros do tratamento térmico de têmpera e revenimento, bem como aplicação de criogenia, na tenacidade a fratura do aço aeronáutico 300M, com a utilização da técnica de corpo cilíndrico com entalhe. Primeiramente, realizou-se a construção da curva de transição dúctil frágil, através de ensaio Charpy, para amostras submetidas a três tratamentos térmicos, 1 - Têmpera seguida de Revenimento, 2 - Têmpera seguida de criogenia e revenimento. Não foi observada influência significativa da aplicação da criogenia (tratamento de numero 2) na curva de transição dúctil-frágil em comparação com o tratamento térmico número 1. Em um segundo momento, com o auxílio da técnica de ensaio de corpo cilíndrico com entalhe, realizou-se a medição da tenacidade à fratura das amostras do aço 300M submetido a quatro diferentes tratamento térmicos, Q, V, C e D. Os tratamentos variavam entre si principalmente pela temperatura de austenitização. Os valores de dureza para as amostras submetidas a criogenia (V e D) foram maiores que as dos tratamentos sem criogenia (Q e C), e também apresentaram tenacidade à fratura menor. Com relação à temperatura de austenitização, observou-se que os tratamentos C e D, austenitizados a 980°C, propiciaram a completa dissolução de precipitados primários da matriz, elevando a tenacidade à fratura com relação aos tratamentos realizados na faixa de 870°C, Q e V, superando também os efeitos negativos para a tenacidade à fratura devido ao aumento no tamanho de grão.
Título en inglés
Fracture toughness determination for 300M aeronautic steel, with different heat treatment parameters and deep cryogenic, using the circumferentially round notched specimens technique
Palabras clave en inglés
300M steel
Aeronautic steel
Circumferentially notched specimen
Fracture toughness
Resumen en inglés
This work studies the influence of the variation for some parameters on quenching and tempering heat treatment, and also deep cryogenic application, on aeronautic steel 300M fracture toughness. First, the ductile-brittle curve was constructed, by Charpy test, for samples submitted for three heat treatments, 1 Quenching and Tempering, 2 Quenching, deep cryogenic and tempering. No significant influence of deep cryogenic treatment addition (heat treatment 2) on ductile-brittle curve was observed in comparison with heat treatment 1. After that, the fracture toughness for 300M steel, submitted for heat treatments Q, V, C e D, was measured using circumferentially notched specimens technique. The main difference among these heat treatments is about austenitizing temperature. For heat treatments with deep cryogenic treatment (V and D), the hardness values were bigger than the ones without this and, analyzing fracture toughness, it was lower than the treatments without cryogenic treatment. Regarding austenitizing temperature, all heat treatments with higher austenitizing temperature at 980°C (C and D), allows complete dissolution of carbides and prior precipitates particles. Its effect was observed that this characteristic increase the fracture toughness when it is compared with others heat treatments with lower austenitizing temperature at 870°C (Q and V). This improvement is enough to overcome the grain size grown negative effects for fracture toughness.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-05-19
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.