Disertación de Maestría
DOI
10.11606/D.18.2017.tde-13012017-091207
Documento
Autor
Nombre completo
Emanoele Maria Santos Chiromito
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2016
Director
Tribunal
Carvalho, Antonio José Felix de (Presidente)
Carvalho, Jonas de
Marini, Juliano
Título en portugués
Preparação de placas rígidas de polpa celulósica e de nanofibras de celulose com polímeros acrílicos
Palabras clave en portugués
Celulose
Nanofibras de celulose
Painéis
PMMA
Resina acrílica
Resumen en portugués
No presente trabalho, foram preparados painéis rígidos compostos de polpa celulósica e nanofibras de celulose (NFC), utilizando como materiais aglomerantes o poli (metacrilato de metila) (PMMA) e uma resina acrílica comercial, empregados em suspensões aquosas do material celulósico e emulsões dos polímeros aglomerantes. Foi desenvolvido um novo método para a preparação dos materiais compósitos baseados em um processo de co-precipitação, onde o reforço de fibras de celulose e o polímero em emulsão são coagulados e isolados da fase aquosa. Foram investigadas misturas de resina/fibra contendo 25%, 50% e 75% de fibras em massa. O grande desafio encontrado foi a obtenção de dispersões homogêneas das fibras nas matrizes acrílicas, uma vez que a natureza hidrofílica da celulose em relação a natureza hidrofóbica das matrizes geralmente leva a separação entre os componentes e a formação de materiais heterogêneos. O processo estudado neste trabalho, conduziu à formação de placas espessas e homogêneas que foram moldadas por prensagem à quente. Os materiais foram caracterizados por meio de ensaios de espectroscopia no infravermelho com transformada de Fourier (FTIR), análise termogravimétrica (TGA), ensaio dinâmico mecânico (DMA), ensaio de tração, absorção de água e microscopia eletrônica de varredura (MEV). As micrografias obtidas por MEV mostraram uma boa dispersão e adesão interfacial das NFC com os materiais acrílicos. Os ensaios de DMA e ensaios de tração evidenciaram o efeito de reforço superior NFC em relação a polpa celulósica. O comportamento dos compósitos obtidos com as NFC foi muito superior do que comportamento dos painéis obtidos com a polpa de celulose. O método desenvolvido para a produção de placas de polímeros acrílicos com altos teores de fibras de celulose se mostrou eficaz, sendo demonstrado o potencial das NFC como material de reforço.
Título en inglés
Preparation and characterization of rigid panels of wood cellulose pulp and nanocellulose with acrilic polymers
Palabras clave en inglés
Acrylic resin
Cellulose
Cellulose nanofibers
Panels
PMMA
Resumen en inglés
In this work, there were prepared rigid panels of poly (methyl methacrylate) (PMMA) and a commercial acrylic resin reinforced with wood pulp and cellulose nanofibers (NFC). Wood pulp and cellulose nanofibers were used from its aqueous suspensions and the thermoplastic polymers used as emulsions. A new method for the preparation of composite materials based on a co-precipitation in which the reinforcement fibers of cellulose and polymer emulsion were coagulated and isolated from the aqueous phase has been developed. Thus, mixtures of resin/fiber containing 25%, 50% and 75% by weight fibers have been investigated. The challenge found to obtain homogenous dispersion of fibers in an acrylic resin matrix, since the hydrophilic nature of the cellulose compared to hydrophobic nature of matrices usually leads to separation of the components and the formation of heterogeneous materials. The process studied in this work led to the formation of thick and homogeneous composites in which were molded by hot pressing. The materials was characterized by Fourier transform infrared spectroscopy (FTIR) thermogravimetric analysis (TGA), dynamical mechanical analysis (DMA), tensile testing, water absorption and scanning electron microscopy (SEM). The SEM micrographs showed good dispersion and interfacial adhesion of NFC with acrylic materials. DMA tests and tensile tests showed higher reinforcing effect NFC in relation to pulp. The method developed for the production of acrylic polymers panels with high cellulose fibers content is effective, being demonstrated the potential of NFC as reinforcing material. The behavior of the panels obtained with NFC was very behavior of the composites obtained from the wood pulp cellulose.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-01-19
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.