Disertación de Maestría
DOI
https://doi.org/10.11606/D.18.2019.tde-14022019-084241
Documento
Autor
Nombre completo
Talita Villa Barbosa
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2018
Director
Tribunal
Branciforti, Márcia Cristina (Presidente)
Dernowsek, Janaina de Andréa
Silveira, Zilda de Castro
Título en portugués
Fabricação de scaffolds de polímero reforçado para aplicação na bioengenharia tecidual
Palabras clave en portugués
Biovidro® 45S5
Manufatura aditiva
Nanofibra de celulose
Poli(ε-caprolactona)
Técnica aditiva por extrusão
Resumen en portugués
No presente trabalho, suportes tridimensionais (scaffolds) de polímero reforçado foram gerados por meio da técnica aditiva por extrusão utilizando duas estratégias de deposição e, posteriormente, foram avaliados morfologicamente, mecanicamente e por meio de ensaios in vitro. Como matriz polimérica do compósito utilizou-se a poli(ε-caprolactona) e como reforço, o Biovidro® 45S5. De forma a melhorar a interação interfacial entre a matriz polimérica e a cerâmica, avaliou-se a incorporação de nanofibra de celulose ao biovidro. Os scaffolds foram fabricados seguindo dois métodos diferentes. O primeiro consistiu no pré-processamento do material em extrusora monorrosca, seguida de extrusão direta na impressora 3D experimental Fab@CTI. O segundo consistiu em um único processo de extrusão diretamente no cabeçote de extrusão. A caracterização química do biovidro por espectroscopia de fluorescência de raios-x mostrou eficiência na preparação da biocerâmica e a caracterização da distribuição do tamanho de partícula por espalhamento de luz dinâmica mostrou a obtenção de partículas submicrométricas. Os scaffolds foram caracterizados morfologicamente pela técnica de microscopia eletrônica de varredura, e, pôde-se notar a eficiência na fabricação de geometrias com arquitetura 00/900 e tamanho de poros adequado para a aplicação na engenharia tecidual. Os ensaios mecânicos de compressão evidenciaram melhoras na rigidez com o aumento do teor de biovidro, no caso dos materiais pré-processados por extrusão, além da influência da nanofibra de celulose na melhoria das propriedades mecânicas. Os ensaios biológicos in vitro mostraram que os scaffolds suportam proliferação celular e que o biovidro é responsável pela maior deposição de sais de cálcio extracelular, facilitando a interação do material sintetizado com o tecido ósseo.
Título en inglés
Manufacture of reinforced polymer scaffolds for application in tissue bioengineering
Palabras clave en inglés
Additive manufacturing
Bioglass® 45S5
Cellulose nanofiber
Extrusion additive technique
Poly (ε-caprolactone)
Resumen en inglés
In the present work, scaffolds of reinforced polymer were generated by means of the extrusion additive technique using two strategies of deposition and, later, were evaluated morphologically, mechanically and by means of in vitro tests. Poly (ε-caprolactone) was used as the polymer matrix of the composite and as a booster, Bioglass® 45S5. In order to improve the interfacial interaction between the polymer matrix and the ceramic, the incorporation of cellulose nanofiber to the bioglass was evaluated. The scaffolds were manufactured following two different methods. The first consisted of the pre-processing of the extruded extruder material followed by direct extrusion into the experimental Fab@CTI 3D printer. The second consisted of a single extrusion process directly on the extrusion head. The chemical characterization of the bioglass by x-ray fluorescence spectroscopy showed efficiency in the preparation of the bioceramics and the characterization of the particle size distribution by dynamic light scattering showed the submicrometric particles. The scaffolds were characterized morphologically by the scanning electron microscopy technique, and it was noted the efficiency in the manufacture of geometries with architecture 00/900 and pore size suitable for application in tissue engineering. The mechanical compression tests showed improvements in stiffness with increasing bioglass content in the case of pre-processed materials by extrusion, as well as the influence of cellulose nanofiber in improving mechanical properties. Biological assays have shown that scaffolds support cell proliferation and that bioglass is responsible for the increased deposition of extracellular calcium salts, facilitating the interaction of the synthesized material with the bone tissue.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2019-02-18
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.