Disertación de Maestría
DOI
10.11606/D.18.2018.tde-15032018-082818
Documento
Autor
Nombre completo
Rafael Paiotti Marcondes Guimarães
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2017
Director
Tribunal
Pinto, Haroldo Cavalcanti (Presidente)
Caram Junior, Rubens
Sandim, Hugo Ricardo Zschommler
Título en portugués
Estudo in situ da solubilização e do envelhecimento da liga β-metaestável Ti-5Al-5Mo-5V-3Cr-1Zr usando difração de raio-X com luz síncrotron de alta energia
Palabras clave en portugués
Difração de raio-X de alta energia
Envelhecimento
Metaestabilidade
Refinamento Rietveld
Ti-55531
Resumen en portugués
Recentemente introduzida no mercado, a liga à base de titânio β-metaestável Ti-5Al-5V-5Mo3Cr-1Zr (Ti-55531) é um material estrutural para aplicações nos setores automotivo e aéreo, além de compor peças para centrífugas. A presente Dissertação de Mestrado tem como objetivo o estudo in situ das transformações de fase em estado sólido da liga Ti-55531 durante o envelhecimento a diferentes temperaturas e condições iniciais por meio de refinamento Rietveld. A ênfase do projeto será a análise qualitativa e quantitativa das principais fases presentes nesta liga, em especial aquelas β de estrutura cúbica de corpo centrado, alfa (α) e ômega (ω) de estrutura hexagonal e martensita (α'') de estrutura ortorrômbica. Os padrões de difração desta liga para os diferentes tempos de envelhecimento foram obtidas com o auxílio da técnica de difração de raio-X de alta energia in situ utilizando luz síncrotron, enquanto que as respectivas análises das imagens dos anéis de difração a partir destes experimentos foram realizadas com o auxílio do programa de integração e calibração instrumental FIT2D e do programa de análise de materiais usando difração (do inglês MAUD).
Título en inglés
In situ study of the annealing and the ageing of the β-metastable Ti-5Al-5Mo-5V-3Cr-1Zr using synchrotron high energy X-ray diffraction
Palabras clave en inglés
Ageing
High energy X-ray diffraction
Metastability
Rietveld refinement
Ti-55531
Resumen en inglés
Recently introduced, the new Ti-55531 titanium based alloy has been developed aiming structural applications such as the automotive and aerospace ones. The present Thesis is focused on the assessment of Ti-55531 alloy in situ solid state transformations during ageing at diferente temperatures as well as initial conditions. In this sense, the study emphasis will deal with both quantitative and qualitative analysis of the main constitutive phases found in the alloy, namely the body-centered cubic β, both hexagonal α and ω and the martensitic α'', this one orthorhombic, by means of Rietveld refinement. Concerning the data, it was obtained by high energy X-ray diffraction (HEXRD) technique in a synchrotron light source facility. All the Debye-Scherrer rings resulting from these in situ experiments were analyzed by both FIT2D and MAUD software.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2018-03-21
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.