Thèse de Doctorat
DOI
10.11606/T.18.2014.tde-16112015-161700
Document
Auteur
Nom complet
Lucíola Lucena de Sousa
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2015
Directeur
Jury
Salomão, Rafael (Président)
Cabrelon, Marcelo Dezena
Fortulan, Carlos Alberto
Marcomini, Raphael Fortes
Morelli, Márcio Raymundo
Titre en portugais
Desenvolvimento e caracterização de cerâmicas porosas moldáveis à base de alumina-mulita para uso como isolamento térmico em altas temperaturas
Mots-clés en portugais
Alumina
Cerâmicas porosas
Hidróxido de alumínio
Mulita
Sinterização
Resumé en portugais
Com o objetivo de reduzir o consumo energético, tem crescido o uso de cerâmicas porosas refratárias como isolantes térmicos para altas temperaturas. Entre as técnicas comumente empregadas na produção desses materiais, destaca-se aquela baseada na geração de poros por meio de transformação de fases. Esse método, que não libera voláteis tóxicos, apresenta uma importante limitação em relação ao uso prolongado em altas temperaturas: os compostos de transição formados após a desidroxilação tendem a acelerar a sinterização, reduzindo a porosidade. É bastante conhecido o fenômeno de que, durante a sinterização em temperaturas elevadas, peças de alumina com alta porosidade, sofrem a eliminação progressiva dos poros presentes. Por essa razão, compostos que dificultam a densificação das peças porosas têm sido adicionados para manter a porosidade originada pela decomposição do hidróxido de alumínio. O objetivo desse trabalho foi obter cerâmicas porosas moldáveis a partir de alumina, hidróxido de alumínio e diversas fontes de sílica (mulita eletrofundida, quartzo e microssílica), utilizando a técnica de decomposição de hidróxidos com o intuito de se formar mulita, composto capaz de diminuir a taxa de densificação em altas temperaturas e com aplicações na indústria petroquímica e do alumínio. As amostras foram sinterizadas entre 1100ºC e 1500ºC e os resultados mostraram que houve aumento da resistência mecânica com a elevação do teor de mulita eletrofundida, quartzo e microssílica incorporada ao sistema. Além disso, o sistema mulita eletrofundida para a composição 0,4-SMT apresentou uma PT = 53,58%, módulo elástico e resistência a compressão (E = 13,03 GPa e σR = 16,83 MPa). O sistema com a adição de quartzo, a amostra 0,2-SQZ, teve pequenas mudanças nos níveis de porosidade (PTG = 59,50%) e não apresentou um elevado aumento do módulo elástico e da resistência a compressão (E = 6,51 GPa e σR = 13,91 MPa) e o sistema contendo microssílica a composição 0,2-SMS apresentou os melhores resultados, tendo um ganho de propriedades mecânicas em temperaturas a 1100ºC e a 1500ºC manteve a porosidade (PTG = 56,23%), reduziu o tamanho médio de poros e apresentou também ótimas propriedades mecânicas (E= 15,39 GPa e σR = 36,79 MPa) proporcionando sua atuação como isolante térmico.
Titre en anglais
Development and characterization of castable porous ceramics based on alumina-mullite for use as thermal insulation in high temperature
Mots-clés en anglais
Alumina
Aluminum hydroxide
Mullite
Porous ceramic
Sintering
Resumé en anglais
Refractory porous ceramics have largely been used as thermal insulators for high temperatures aiming to reduce energy consumption. The generation of pores through phase transformation (such as Al(OH)3 dehydroxilation) is one of the most interesting techniques employed to produce such materials. This method, which does not release toxic volatile, imposes an important limitation on the prolonged use at high temperatures. The transition compounds formed after the dehydroxylation tend to accelerate sintering and reduce porosity. It is well known that during sintering at high temperatures (above 1100ºC), parts of alumina with high porosity amounts undergo gradual pores' elimination. Therefore, compounds that hinder densification of porous pieces have been added to these compositions in order to maintain the porosity generated by the decomposition of aluminum hydroxide. This thesis addresses the production of castables porous ceramics from alumina, aluminum hydroxide and different sources of silica (electrofuse mullite, quartz and microsilica), employed for the in situ formation of mullite, a compound that reduces the rate of densification at high temperatures. The applications include petrochemical and aluminum industries. Samples were sintered between 1100ºC and 1500ºC and the results of the systems which contained electrofused mullite, quartz and microsilica showed less intense porosity levels reduction. The system with addition of electrofused mullite showed PTG = 53,58%,E = 13,03 GPa and σR = 16,83 MPa. The system containing quartz, presented a lower change of porosity (PTG = 59,50%) and the system containing microsilica provided the best results and an increment in the mechanical properties at temperatures between 1100°C and 1500°C. This last system also kept porosity (PTG = 56,23%), and reduced the average pore size. Its good mechanical properties (E = 15,39 GPa and σR = 36,79 MPa) proved it can be used as a thermal insulator.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Luciolatese.pdf (10.64 Mbytes)
Date de Publication
2015-11-23
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.