• JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
  • JoomlaWorks Simple Image Rotator
 
  Bookmark and Share
 
 
Disertación de Maestría
DOI
https://doi.org/10.11606/D.18.2017.tde-17112017-104317
Documento
Autor
Nombre completo
Monica Costa Rodrigues Guimarães
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2017
Director
Tribunal
Pinto, Haroldo Cavalcanti (Presidente)
Alvarez, Fernando
Souza, Roberto Martins de
Título en portugués
Deposição e caracterização de filmes finos de CrN depositados por diferentes processos de magnetron sputtering
Palabras clave en portugués
Magnetron Sputtering
CrN
Filmes finos
HiPIMS
Resumen en portugués
O PVD (Physical Vapor Deposition- Deposição física na fase de vapor) é um meio utilizado para a produção de recobrimentos e empregado em grande escala industrial. É um processo de deposição atômica no qual o material é vaporizado de alvo sólido por sputtering e posteriormente condensado sobre a peça a ser revestida na forma de filme. O processo ocorre em uma câmara de vácuo, na presença de plasma, e por diferença de potencial os íons, na forma pura ou combinados com átomos de hidrogênio ou carbono, são movidos para a superfície do substrato. Uma técnica relativamente nova de sputtering é o HiPIMS (High Power Impulse Magnetron Sputtering) que utiliza impulsos de energia extremamente altas com densidade de potência possibilitando filmes com melhores performances e mais densos. No presente trabalho filmes de nitreto de cromo (CrN) foram depositados por duas técnicas de magnetron sputtering, HiPIMS e DCMS (Direct Current Magnetron Sputtering), variando frequência de pulso em 400 Hz, 450 Hz e 500 Hz para o HiPIMS e a tensão de polarização em 0 V, -20 V, -40V, -60V, - 100 V e -140 V para os dois processos. Foram obtidos filmes com maior dureza, menor rugosidade para HiPIMS, no entanto DCMS apresentou maior taxa de deposição. O aumento da frequência nos filmes HiPIMS, assim como o aumento da tensão de polarização negativa possibilitaram filmes com morfologia mais densa e homogênea. Este fato também foi observado com o aumento do valor de bias nos filmes depositados por DCMS. Os valores de dureza obtidos (17 ± 2 para DCMS e 26 ± 1 para HiPIMS) são superiores aos reportados na literatura e podem estar relacionados ao efeito de "multicamadas" obtido pela oscilação do substrato.
Título en inglés
Deposition and characterization of CrN thin films deposited by different magnetron sputtering processes
Palabras clave en inglés
CrN
HiPIMS
Magnetron sputtering
Thin films
Resumen en inglés
PVD (Physical Vapor Deposition) is a process used for coatings deposition and it is used on a large industrial scale. It is an atomic deposition process in which the material is vaporized from solid target by sputtering and then condensed onto the part to be coated in film form. The process occurs in a vacuum chamber in the presence of plasma, and by potential difference the ions in pure form or combined with hydrogen or carbon atoms are moved to the surface of the substrate. A relatively new sputtering technique is the HiPIMS (High Power Impulse Magnetron Sputtering) which uses extremely high energy pulses with power density to enable higher performance and denser films. In the present work, chromium nitride (CrN) films were deposited by two magnetron sputtering techniques, HiPIMS and DCMS (Direct Current Magnetron Sputtering), varying the pulse frequency at 400 Hz, 450 Hz and 500 Hz for the HiPIMS and the bias at 0 V, -20 V, -40 V, -60 V, -100 V and -140 V for both processes. It was obtained films with high hardness, less roughness for HiPIMS, however DCMS presented a higher rate of deposition. The increase of the frequency in the HiPIMS films, as well as the increase of the negative polarization voltage, allowed films with denser and homogeneous morphology. This fact was also observed with the increase of the value in the films deposited by DCMS. The hardness values obtained (17 ± 2 for DCMS and 26 ± 1 for HiPIMS) were higher than those reported in the literature and may be related to the "multilayer" effect obtained by substrate oscillation.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2017-11-20
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.