Disertación de Maestría
DOI
Documento
Autor
Nombre completo
Yajaira Dalila Rivero Jerez
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2018
Director
Tribunal
Mastelaro, Valmor Roberto (Presidente)
Maia, Lauro June Queiroz
Silva, Luis Fernando da
Título en portugués
Efeito dos parâmetros de síntese e da adição de alumínio na propriedade de fotoluminescência do composto SrTiO3
Palabras clave en portugués
Alumínio
fotoluminescência
Pechini
Perovskita
Raman
SrTiO3
tempo de vida
XANES
Resumen en portugués
O titanato de estrôncio (SrTiO3) é um material de estrutura perovskita que tem sido extensivamente estudado, principalmente no que tange sua propriedade fotoluminescente. Os resultados presentes na literatura mostram que a intensidade fotoluminescente pode depender de muitas variáveis como o estado físico do material, dos precursores utilizados na síntese e da adição de íons dopantes. Apesar dos compostos de estrutura perovskita e em especial do composto SrTiO3 ter sido muito bem estudado no que tange sua propriedade fotoluminescente, ao nosso conhecimento, o efeito da pureza da água utilizada e da adição do alumínio em substituição ao titânio sobre esta propriedade ainda não foi estudada. Para atingir este objetivo, amostras de composição SrTi1-xAlxO3 com x variando de 0.005, 0.01, 0.03 e 0.05 foram preparadas através do método dos precursores poliméricos modificado. As amostras foram caracterizadas por análise térmica, difração de raios X (XRD), espectroscopia Raman, espectroscopia de absorção de raios X (XANES), espectroscopia de fotoluminescência (PL) e medidas de tempo de vida. Estudos sobre os efeitos da temperatura e tempo de calcinação, pureza da agua e quantidade de alumínio nas propriedades fotoluminescentes foram realizados. De uma maneira geral, observou-se que o uso da água ultra-pura (Milli-Q) e da adição de 0,5 % em mol de alumínio aumenta a atividade fotoluminescente do material.
Título en inglés
Effect of synthesis parameters and Aluminum addition on the photoluminescent property of the SrTiO3 compound
Palabras clave en inglés
Aluminum
lifetime
Pechini
Perovskite
Photoluminescence
raman
SrTiO3
XANES
Resumen en inglés
Strontium titanate (SrTiO3) is a material of perovskite structure that has been extensively studied, mainly with regard to its photoluminescent property. The results in the literature show that the photoluminescent intensity may depend on many variables such as the physical state of the material, the precursors used in the synthesis and the addition of dopant ions. Although the compounds of the perovskite structure and in particular the compound of SrTiO3 have been very well studied with respect to their photoluminescent property, to our knowledge, the effect of the purity of the water used and the addition of the aluminum in substitution for the titanium on this property has not yet been studied. To achieve this goal, samples of SrTi1-xAlxO3 composition with x ranging from 0.005, 0.01, 0.03 and 0.05 were prepared by the modified polymer precursor method. The samples were characterized by thermal analysis, X-ray diffraction (XRD), Raman spectroscopy, X-ray absorption spectroscopy (XANES), photoluminescence (PL) spectroscopy and lifetime measurements. Studies on the effects of temperature and calcination time, water purity and amount of aluminum on the photoluminescent properties were performed. In general, it was observed that the use of high purity (Milli-Q) water and the addition of 0.5 mol% of aluminum improves the photoluminescent activity of the material.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2019-06-11
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2019. Todos los derechos reservados.