Mémoire de Maîtrise
DOI
10.11606/D.18.2015.tde-22092015-105627
Document
Auteur
Nom complet
Sabrina Nicoleti Carvalho dos Santos
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2015
Directeur
Jury
Gonçalves, Débora (Président)
Gonçalves, Raquel
Lahr, Francisco Antonio Rocco
Titre en portugais
Análise estrutural e de superfície de madeiras submetidas a tratamento térmico e degradadas pelo fungo Pycnoporus sanguineus
Mots-clés en portugais
Análise dinâmico-mecânica
Ângulo de contato
Madeira
Raios X
Tratamento térmico
Resumé en portugais
Neste trabalho, analisou-se como o tratamento térmico e a degradação pelo fungo de podridão branca influenciaram as propriedades dos componentes das amostras de madeira das espécies Araucaria sp., Pinus sp., Erisma sp. e Hymenaea sp.. Essas amostras foram cortadas em diferentes planos de corte e submetidas inicialmente a um teor de umidade de equilíbrio de 12%. As caracterizações das amostras foram realizadas empregando a técnica de ângulo de contato, medidas de perda de massa (somente para amostras degradadas pelo fungo), a análise dinâmico-mecânica (DMA) e difração de raios X. Para as amostras degradadas pelo fungo, o valor de perda de massa foi maior para a espécie Pinus sp. e menor para Hymenaea sp.. Os difratogramas de raios X apontaram que o corte transversal apresentou um caráter mais amorfo em relação ao corte longitudinal. As medidas de ângulo de contato mostraram que com o aumento da temperatura de tratamento térmico a superfície se tornou mais hidrofóbica. O mesmo comportamento foi verificado para amostras submetidas à degradação pelo fungo. De forma que, tanto o tratamento térmico quanto a degradação pelo fungo, ocasionaram um aumento de grupos não-polares presentes na superfície. Já nas medidas de DMA foi observado que o módulo de armazenamento (E') diminuiu com o aumento da temperatura. E o grau de mobilidade das cadeias poliméricas foi analisado por meio das temperaturas de transições vítreas das hemiceluloses e lignina (Tg), bem como, as relaxações secundárias através do fator de perda (tan δ). Esses resultados possibilitam uma maior elucidação sobre como o tratamento térmico e a degradação fúngica afetam diferentes tipos de amostras de várias espécies de madeira, essas informações são relevantes para a utilização e preservação dessas madeiras.
Titre en anglais
Structural analysis and surface of wood heat-treated and degraded by the fungus Pycnoporus sanguineus
Mots-clés en anglais
Contact angle
Dynamic-mechanical analysis
Heat treatment
Wood
X-ray
Resumé en anglais
The present dissertation addresses the analysis of the influence of heat treatment and degradation by white rot fungus on the properties of the components of wood species Araucaria sp., Pinus sp., Erisma sp. and Hymenaea sp. Samples were cut at different cutting plans and initially subjected to a 12% equilibrium moisture content. They were then characterized by a contact angle technique, weight loss measurements (for samples degraded by the fungus), dynamic mechanical analysis (DMA) and X-ray diffraction. The mass loss values of samples degraded by the fungus were higher for Pinus sp. and lower for Hymenaea sp. The X-ray diffraction showed the transversal cut had an amorphous character in relation to the longitudinal cut. According to the contact angle measurements, showed that with increasing heat treatment temperature over the surface became hydrophobic. The same behavior was observed for samples submitted to degradation by fungus. In order, that both heat treatment and degradation by the fungus, caused an increase of non-polar groups on the surface. The DMA measurements showed the storage modulus (E') decreases with increasing temperature. The degree of mobility of the polymer chains was analyzed through glass transition temperatures of hemicelluloses and lignin (Tg) and the secondary relaxations were assessed through the loss factor (tan δ). The results enabled greater elucidation on how the heat treatment and fungal degradation affect different types of samples of various wood species. Such information is relevant for the use and preservation of woods.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2015-09-25
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2021. Tous droits réservés.