Tesis Doctoral
DOI
https://doi.org/10.11606/T.18.2016.tde-25102016-110245
Documento
Autor
Nombre completo
Adriane Damasceno Vieira de Souza
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Carlos, 2016
Director
Tribunal
Salomão, Rafael (Presidente)
Andreeta, Marcello Rubens Barsi
Bernardi, Maria Inês Basso
Cabrelon, Marcelo Dezena
Oliveira, Ivone Regina de
Título en portugués
Evolução microestrutural e de propriedades físicas de cerâmicas porosas moldáveis de alta alumina durante calcinação e sinterização
Palabras clave en portugués
Alumina calcinada
Alumina hidratável
Cerâmicas porosas
Hidróxido de alumínio
Microestrutura
Resumen en portugués
A combinação de óxido de alumínio (Al2O3) com hidróxido de alumínio (Al(OH)3) resulta numa maneira interessante de produzir cerâmicas porosas com baixa condutividade térmica, alta área superficial específica, elevada refratariedade e estabilidade química, com custos competitivos. Devido a essas características, esse sistema tem grande potencial de aplicação tecnológica em catalisadores, isolantes térmicos e filtros para altas temperaturas. Apesar do bom desempenho, essas cerâmicas ainda apresentam limitações tais como a baixa resistência termomecânica, devido à elevada porosidade (principalmente, naqueles materiais com fração volumétrica de poros acima de 50%) e redução de porosidade causada pelos fenômenos de sinterização e crescimento de grãos que se intensificam acima de 1100°C. Por esse motivo, investigações adicionais são necessárias a fim de minimizar esses aspectos negativos. Este trabalho teve como objetivo desenvolver estruturas porosas moldáveis (porosidade acima de 50%) de alta alumina, com adequada resistência mecânica (acima de 10 MPa em compressão) e que fossem resistentes à densificação, para uso em temperaturas acima de 1100°C. Inicialmente foi realizado um estudo sobre a decomposição térmica (temperatura variando de 300°C a 1500°C) de três tipos de hidróxidos de alumínio com diferentes granulometrias (1, 10 e 100 µm) a fim de avaliar seus potencias como agentes porogênicos. Em seguida, por meio de ensaios reológicos, determinou-se as condições ideais de dispersão e mistura das partículas de alumina calcinada, hidróxido de alumínio e alumina hidratável. Em uma segunda etapa do trabalho, suspensões aquosas de alumina calcinada (D50: 1 µm ou 2,5 µm) consolidadas com alumina hidratável foram preparadas com diferentes proporções (0 - 67,5% vol.) de Al(OH)3 (D50: 1 µm ). Para os tipos de Al(OH)3 com partículas maiores foram preparadas somente as composições contendo 22,5% vol. de alumina calcinada (2,5 µm), 67,5% de hidróxido de alumínio e 10% vol. de alumina hidratável. As amostras foram submetidas a tratamentos térmicos em 1100°C, 1300°C e 1500°C durante 3 h. O comportamento durante a sinterização foi acompanhado por meio de dilatometria e as estruturas verdes/secas e sinterizadas foram caracterizadas em relação à porosidade total e tamanho médio dos poros, resistência à compressão e módulo elástico. A evolução da microestrutura foi avaliada usando microscopia eletrônica de varredura. Comprovou-se a ação porogênica do Al(OH)3 em matrizes de alumina calcinada. Essa ação depende de diversos fatores como teor adicionado, temperatura máxima de sinterização e da relação entre as granulometrias da matriz e do Al(OH)3. Variando-se esses parâmetros, estruturas com elevada porosidade (acima de 50%) e resistência à ruptura por compressão (acima de 10 MPa) foram obtidas. Foi observado que a alumina hidratável, utilizada como ligante, desempenha papel de grande importância no desenvolvimento da microestrutura desses materiais, particularmente em temperaturas abaixo de 1000°C.
Título en inglés
Evolution of the microstructure and the physical properties of high-alumina-based castable porous ceramics during calcination and sintering
Palabras clave en inglés
Aluminium Hydroxide
Calcined Alumina
Hydratable Alumina
Microstructure
Porous ceramics
Resumen en inglés
The combination of aluminum oxide (Al2O3) and aluminum hydroxide (Al(OH)3) results in an interesting way of producing porous ceramics of low thermal conductivity, high specific surface area, high refractoriness, and chemical stability at competitive costs. Consequently, such a system shows great potential for technological applications in catalysts, thermal insulators and filters for high temperatures. Despite the good performance of those ceramics, they still have limitations, as low thermomechanical strength, due to high porosity (especially materials whose volume fraction of pores exceeds 50%) and reduced porosity caused by the sintering phenomena and grain growth intensified above 1100°C. Therefore, further research is required for the minimization of such negative aspects. This thesis addresses the development of moldable porous structures (porosity higher than 50%) of high alumina with proper mechanical strength (above 10 MPa in compression) and densification resistance, for use at temperatures above 1100°C. First, a study on the thermal decomposition (temperatures ranging from 300°C to 1500°C) of three types of aluminum hydroxides of different granulometries (1, 10 e 100 µm) was conducted for the evaluation of their potential as porogenic agents. Rheological measurements enabled the determination of the optimal conditions for the dispersion and mixing of the calcined alumina particles, hydratable alumina and aluminum hydroxide. In a second stage of the study, aqueous suspensions of calcined alumina (D50: 1 µm ou 2.5 µm) consolidated with hydratable alumina were prepared with different proportions (0 - 67.5 vol.%) of Al(OH)3 (D50: 1 µm ). However, for Al(OH)3 with larger particles, were only prepared compositions with 22.5 vol.% of calcined alumina (2.5 µm), 67.5 vol.% of aluminum hydroxide, and 10 vol.% of hydratable alumina. The samples were heat treated at 1100, 1300 and 1500°C for 3 h. The behavior during sintering was studied by dilatometry and the green/dried and sintered structures were characterized regarding the total porosity and average pore size, compressive strength and elastic modulus. The evolution of the microstructure was evaluated by scanning electron microscopy. The porogenic action of Al(OH)3 on a calcined alumina matrix was proved and showed to depend on several factors, as content added, maximum sintering temperature and relationship between the grain size of the matrix and Al(OH)3. Variations in those parameters yielded structures of high porosity (higher than 50%) and resistance to compression fracture (above 10 MPa). The hydratable alumina used as a binder played a major role in the development of the microstructure of such materials, particularly at temperatures below 1000°C.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2016-10-26
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
CeTI-SC/STI
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2024. Todos los derechos reservados.