Mémoire de Maîtrise
DOI
10.11606/D.18.2014.tde-29012015-215637
Document
Auteur
Nom complet
Marcelo Rizzo Piton
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Carlos, 2014
Directeur
Jury
Mastelaro, Valmor Roberto (Président)
Lisboa Filho, Paulo Noronha
Silva, Elson Longo da
Titre en portugais
Síntese e caracterização do composto SrTi1-xMnxO3 nanoestruturado
Mots-clés en portugais
Fotoluminescência
Manganês
Precursores poliméricos
SrTiO3
XANES
Resumé en portugais
Amostras nanoestruturadas do sistema SrTi1-xMnxO3 (STM) com x = 0%, 0.5%, 1%, 2.5%, 5% e 10% na forma de pó foram sintetizadas através do método dos precursores poliméricos. As propriedades térmicas, estruturais e ópticas das amostras STM calcinadas em diferentes temperaturas foram analisadas a temperatura ambiente através de técnicas de análise térmica, difração de raios-x, espectroscopia de absorção de raios-x e fotoluminescência. Os resultados obtidos através das técnicas de analise térmica mostraram que o íon manganês causa um efeito retardante, aumentando a temperatura onde ocorre o início da cristalização. Os resultados de DRX mostraram que no limite de solubilidade estudado, o íon manganês foi incorporado em solução sólida no sítio B na rede do SrTiO3 (ST), assumindo estados de oxidação entre +3,4 e +3,7, indicando que ocorre a criação de defeitos para compensação de cargas, mantendo a neutralidade elétrica do material. A análise dos espectros de fotoluminescência das amostras STM amorfas mostrou que o aumento da quantidade de manganês até 1% leva a um aumento da intensidade fotoluminescência em relação a amostra SrTiO3. Entretanto, a adição de manganês acima desta quantidade leva a uma diminuição pronunciada da intensidade fotoluminescente. Nas amostras amorfas não foi observada uma variação significativa da ordem local ao redor dos átomos de titânio bem como no estado de oxidação dos átomos de manganês à medida que a quantidade de manganês aumenta. Desta forma, a variação da intensidade fotoluminescente não pôde ser atribuída a estes fatores. O aumento da temperatura de calcinação leva a uma diminuição significativa da intensidade fotoluminescente. Uma análise dos espectros XANES medidos na borda K do titânio destas amostras mostrou que ocorre uma maior ordenação dos átomos de Ti nos octaedros de oxigênio [TiO6] a medida que a temperatura de calcinação aumenta, ou seja, à medida que aumenta o grau de cristalinidade das amostras.
Titre en anglais
Synthesis and characterization of nanostructured SrTi1-xMnxO3 compound
Mots-clés en anglais
Manganese
Photoluminescence
Polymeric precursor method
SrTiO3
XANES
Resumé en anglais
Nanostructured SrTi1-xMnxO3 (STM) powder samples with x = 0%, 0.5%, 1%, 2.5%, 5% and 10% were synthesized by the polymeric precursors method. The thermal, structural and optical properties of STM samples heat-treated at different temperatures were analyzed by thermal analysis, X-ray diffraction, X-ray absorption spectroscopy and photoluminescence techniques. The thermal analysis results have shown that manganese ion causes a retarding effect, increasing the onset of the crystallization temperature. The XRD results showed that manganese ion is incorporated in a solid solution in the B site of the SrTiO3 (ST) network for the range of solubility studied, with oxidation states between +3.4 and +3.7, indicating the creation of charge compensation defects, keeping the materials electrical neutrality. The analysis of the photoluminescence (PL) spectra of the STM amorphous samples showed that the PL intensity increases when the amount of manganese is up to 1%. However, higher manganese concentrations leads to a pronounced decrease of the photoluminescence intensity. The amorphous samples showed no significant change of the local order around the titanium atoms, observed as well as in the oxidation state of the manganese atoms as the amount of manganese increases. Thus, the variation of the photoluminescence intensity cannot be explained by these factors. Increasing the calcination temperature leads to a significant decrease of the photoluminescence intensity. An analysis of the XANES spectra measured at the titanium K edge of these samples showed that as the calcination temperature increases, i. e., as it increases the degree of crystallinity, the ordering of the Ti atoms in the oxygen octahedra TiO6 of the samples increases.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2015-02-11
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.