Tese de Doutorado
DOI
10.11606/T.23.2013.tde-04092013-153641
Documento
Autor
Nome completo
Tathiane Larissa Lenzi
E-mail
Unidade da USP
Área do Conhecimento
Data de Defesa
Imprenta
São Paulo, 2013
Orientador
Banca examinadora
Raggio, Daniela Prócida (Presidente)
Imparato, Jose Carlos Pettorossi
Mendes, Fausto Medeiros
Rocha, Rachel de Oliveira
Sanabe, Mariane Emi
Título em português
Efeito da condição do substrato e do tempo de condicionamento na estabilidade da união de sistemas adesivos à dentina de dentes decíduos
Palavras-chave em português
Adesivos dentinários
Cárie dentária Microscopia eletrônica de varredura
Dente decíduo
Dentina
Resistência à tração
Resumo em português
Este estudo objetivou investigar a influência da redução do tempo de condicionamento na união de sistemas adesivos à dentina hígida e afetada por cárie de dentes decíduos, por meio de testes de microtração, nanoinfiltração e avaliação micromorfológica da interface adesiva. A superfície dentinária de 48 segundos molares decíduos foi exposta e os dentes divididos aleatoriamente em 8 grupos experimentais de acordo com o substrato (dentina hígida e afetada por cárie ciclagem de pH por 14 dias), sistema adesivo (Adper Single Bond 2 adesivo convencional de dois passos e Clearfil SE Bond - sistema autocondicionante de dois passos) e tempo de condicionamento (recomendado pelo fabricante e metade do tempo). Desta forma, o adesivo Adper Single Bond 2 foi aplicado à dentina após condicionamento com ácido fosfórico a 35% por 15 ou 7 segundos e o agente de união do Clearfil SE Bond após 20 ou 10 segundos de aplicação do primer. Blocos de resina composta (Filtek Z250) foram confeccionados e, após 24 horas de armazenamento em água destilada, os dentes foram seccionados para obtenção de espécimes com área de secção transversal de aproximadamente 0,8 mm2. Metade dos espécimes foi submetida imediatamente ao teste de microtração e a outra metade após 12 meses de armazenamento em água destilada. O padrão de fratura foi avaliado em estereomicroscópio com aumento de 400x. Dois espécimes de cada dente nos respectivos períodos de armazenamento foram imersos em nitrato de prata amoniacal por 24 horas e revelados (8 horas) para avaliação da nanoinfiltração em microscopia eletrônica de varredura. Adicionalmente, dois dentes para cada grupo experimental (n=16) foram preparados como descrito para o teste de microtração e seccionados perpendicularmente à interface adesiva, após 24 horas, para análise da micromorfologia e espessura da camada híbrida. Os valores de resistência de união, expressos em megapascal (MPa), foram submetidos à Análise de Variância (ANOVA) e teste de Tukey ( = 0,05). As demais avaliações foram descritivas. Os sistemas adesivos apresentaram valores similares de resistência de união imediata. Decréscimo dos valores de resistência de união ocorreu após 12 meses de armazenamento em água, exceto para o adesivo Clearfil SE Bond em substrato hígido. A adesão à dentina afetada foi menor em comparação à dentina hígida. A nanoinfiltração também foi mais pronunciada neste substrato. O tempo de condicionamento influenciou apenas a adesão do sistema adesivo Adper Single Bond 2. Maiores valores de resistência de união e menor infiltração de nitrato de prata na interface adesiva foram observados quando o tempo de condicionamento ácido foi reduzido pela metade, independente do substrato. Camadas híbridas mais finas foram produzidas quando a dentina decídua foi condicionada por 7 segundos, especialmente em dentina afetada. Predomínio de fratura adesiva/mista foi observado para todos os grupos experimentais. Em conclusão, o efeito da redução no tempo de condicionamento é material dependente e resulta em maior estabilidade da união de sistema adesivo convencional de dois passos à dentina hígida e afetada de dentes decíduos.
Título em inglês
Effect of substrate condition and etching time on the bonds stability of adhesive systems to dentin of primary teeth
Palavras-chave em inglês
Deciduous tooth
Dental caries
Dentin
Dentin-bonding agents
Scanning electron microscopy
Tensile strength
Resumo em inglês
This study aimed to investigate the influence of shortening the etching time on bond of adhesive systems to sound and caries-affected dentin of primary teeth by microtensile and nanoleakage tests, and micromorphological evaluation of the adhesive interface. The dentinal surface of 48 second primary molars was exposed and the teeth were randomly assigned to 8 experimental groups according to substrate (sound and caries-affected dentin - pH-cycling for 14 days), adhesive system (Adper Single Bond 2 two-step etch-and-rinse adhesive system and Clearfil SE Bond two step self-etch adhesive system) and etching time (recommend by manufacturers and half-reduced time). Thus, the adhesive Adper Single Bond 2 was applied to dentin after 35% phosphoric acid etching for 15 or 7 seconds, and the bond of Clearfil SE Bond after 20 or 10 seconds of primer application. Composite resin blocks (Filtek Z250) were built and, after 24 hours of storage in distilled water, the teeth were sectioned to obtain specimens with cross-sectional area of approximately 0.8 mm2. Half of the specimens were immediately subjected to microtensile test and the other half after 12 months of storage in distilled water. The fracture pattern was evaluated with a stereomicroscope at 400x magnification. Two specimens from each tooth in the respective storage periods were immersed in ammoniacal silver nitrate for 24 hours and revealed (8 hours) to evaluate the nanoleakage in scanning electron microscope. Additionally, two teeth for each experimental group (n=16) were prepared as described for the microtensile test and perpendicularly sectioned to the adhesive interface, after 24 hours, for analysis of micromorphology and thickness of the hybrid layer. Bond strength values, expressed in megapascal (MPa), were submitted to Analysis of Variance (ANOVA) and Tukeys tests ( = 0.05). Other evaluations were descriptive. The adhesive systems presented similar immediate bond strength values. A decrease in bond strength values occurred after 12 months of water storage, except for Clearfil SE Bond in sound substrate. Bonding to caries-affected dentin was lower compared to sound dentin. The nanoleakage was also more pronounced in this substrate. Etching time only influenced the bonding of the adhesive system Adper Single Bond 2. Higher bond strength values and lower infiltration of silver nitrate into adhesive interface were observed when the etching time was half-reduced, irrespective of the substrate. Thinner hybrid layers were produced when the primary dentin was acid etched for 7 seconds, especially in caries-affected dentin. Predominance of adhesive/mixed fracture was observed for all experimental groups. In conclusion, the effect of shortening the etching time is material dependent and results in higher bond stability of two-step etch-and-rinse adhesive system to sound and caries-affected dentin of primary teeth.
 
AVISO - A consulta a este documento fica condicionada na aceitação das seguintes condições de uso:
Este trabalho é somente para uso privado de atividades de pesquisa e ensino. Não é autorizada sua reprodução para quaisquer fins lucrativos. Esta reserva de direitos abrange a todos os dados do documento bem como seu conteúdo. Na utilização ou citação de partes do documento é obrigatório mencionar nome da pessoa autora do trabalho.
Data de Publicação
2013-10-23
 
AVISO: O material descrito abaixo refere-se a trabalhos decorrentes desta tese ou dissertação. O conteúdo desses trabalhos é de inteira responsabilidade do autor da tese ou dissertação.
  • ALVES, F. B. T., et al. Bonding of Simplified Adhesive Systems to Caries-affected Dentin of Primary Teeth. Journal of Adhesive Dentistry, 2013, vol. xx, p. 2013 Jan 16-xxx.
  • ALVES, F. B. T., et al. The bonding of glass ionomer cements to caries-affected primary dentin. Pediatric Dentistry, 2013, vol. 35, p. 320-324.
  • BONINI, G. A. V. C., et al. Reparo de restauração de amálgama em dente decíduo: relato de caso clínico. Revista da Associação Paulista de Cirurgiões Dentistas (Cessou em 1980. Cont. ISSN 0101-8140 Revista Regional de Araçatuba - Associação Paulista de Ci, 2011, vol. 65, p. 228-233.
  • CRUZ JB, et al. Eroded dentin does not jeopardize the bond strength of adhesive restorative materials. Brazilian Oral Research , 2012, vol. 45, p. 01-07.
  • GUGLIELMI, CAMILA ALMEIDA BRANDÃO, et al. Influence of ultrasound or halogen light on microleakage and hardness of enamel adjacent to glass ionomer cement [doi:10.1111/j.1365-263X.2011.01173.x]. International Journal of Paediatric Dentistry [online], 2012, vol. 22, p. 110-115.
  • LENZI, T. L., et al. Bond strength of high viscous glass ionomer cements primary dentin. IJD. International Journal of Dentistry, 2011, vol. 10, p. 5-9.
  • LENZI, T. L., et al. Effect of shortening the etching time on bonding to sound and caries-affected dentin of primary teeth. Pediatric Dentistry, 2013.
  • LENZI, T. L., et al. Flowable glass ionomer cement layer bonding to sound and carious primary dentin. Journal of dentistry for children (Chicago, Ill.) (Cessou em 2006. Cont. ISSN 1935-5068 Journal of dentistry for children (Chicago, Ill. Online)), 2013, vol. 80, p. 20-24.
  • LENZI, T. L., et al. Perfil dos ciruriões-dentistas integrantes do Programa Saúde da Família em um município do Sul do Brasil. Revista do Instituto de Ciências da Saúde (UNIP), 2010, vol. 28, p. 121-124.
  • LENZI, T. L., et al. Repairing ditched amalgam restorations is less time and tooth structure-consuming than replacement. European Archives of Paediatric Dentistry , 2013, vol. xx, p. xx-xx.
  • LENZI, T. L., et al. Tubule Density and Diameter in Coronal Dentin from. Microscopy and Microanalysis , 2013, vol. 15, p. 1-5.
  • LENZI, TATHIANE L., et al. Shear bond strength of two adhesive materials to eroded enamel. The Journal of Contemporary Dental Practice, 2013.
  • LENZI, TATHIANE LARISSA, et al. One-step self-etch adhesive bonding to pre-etched primary and permanent enamel. Journal of Dentistry for Children (Chicago, Ill. Online), 2013, vol. 80, p. 57-61.
  • Raggio, Daniela P., et al. Is Atraumatic restorative treatment an option for restoring occlusoproximal caries lesions in primary teeth? A systematic review and meta-analysis [doi:10.1111/ipd.12013]. International Journal of Paediatric dentistry [online], 2012, vol. xxx, p. n/a-n/a.
  • ALVES, F. B. T., et al. Adhesive systems bonding to caries-affected dentine in primary teeth. In 23rd Congress of International Association of Paediatric Dentistry, Atenas, 2011. International Journal of Paediatric dentistry ., 2011. Abstract.
  • GUGLIELMI, C. B., et al. Glass ionomer dement bonding to primary dentine after two methods of insertion. In 23rd Congress of International Association of Paediatric Dentistry, Atenas, 2011. International Journal of Paediatric dentistry ., 2011. Abstract.
Todos os direitos da tese/dissertação são de seus autores
Centro de Informática de São Carlos
Biblioteca Digital de Teses e Dissertações da USP. Copyright © 2001-2020. Todos os direitos reservados.