Thèse de Doctorat
DOI
10.11606/T.23.2004.tde-01032005-155422
Document
Auteur
Nom complet
Anna Liubushka Olivera Belsuzarri
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2004
Directeur
Jury
Marques, Marcia Martins (Président)
Matson, Mauricio Rufaiel
Oliveira, Denise Cerqueira
Russo, Eliza Maria Agueda
Saito, Tetsuo
Titre en portugais
Efeito das superfícies cerâmicas no desgaste do esmalte dos dentes antagonistas.
Mots-clés en portugais
Cerâmicas
Esmalte
Rugosidade superficial
Resumé en portugais
O efeito das superfícies cerâmicas no desgaste do esmalte antagonista foi estudado in vitro. Foram avaliados os desgastes produzidos pelas porcelanas glazeadas e polidas. Para tal finalidade utilizaram-se cinco cerâmicas: IPS Empress 2 (Ivoclar),IPS Empress (Ivoclar), Duceram Plus (Degussa), Duceram LFC (Degussa) e Symbio (Degussa). Oito conjuntos dente e cerâmica foram testados para cada situação, com carga padronizada e imersos em água a 37 0 C. As medidas do desgaste do esmalte e cerâmica foram avaliadas após 150000 e 300000 ciclos. Os resultados revelaram que o desgaste final do esmalte do dente antagonista foi significantemente menor quando as cerâmicas foram polidas. A quantidade do desgaste do esmalte antagonista foi maior nos primeiros 150000 ciclos. A cerâmica IPS Empress provocou um desgaste significativamente maior do esmalte do dente antagonista quando comparada com as outras cerâmicas testadas (p<0,01). As rugosidades iniciais das superfícies cerâmicas foram diferentes entre si, sendo que diminuíram após o polimento, exceto para a cerâmica IPS Empress. Não houve correlação entre a rugosidade superficial inicial das cerâmicas com o desgaste gerado no esmalte dos dentes antagonistas.
Titre en anglais
The effect of glazed and polished ceramics on the wear of human enamel.
Mots-clés en anglais
Ceramic
Enamel
Roughness
Wear
Resumé en anglais
The effect of glazed and polish dental ceramic on the wear of human enamel was studied in vitro. Five ceramics: IPS Empress 2 (Ivoclar), IPS Empress (Ivoclar),Duceram Plus (Degussa), Duceram LFC (Degussa) and Symbio (Degussa), were tested in water at 37 0 C, under standard load. The amount of wear enamel and specimens was determined after 150000 and 300000 cycles. The results showed that the polished ceramics produce less amount of enamel wear. The amount of enamel wear opposite to IPS Empress ceramic was significant higher (p<0,001). The enamel wear rate increased on the first 150000 cycles. Differences between roughnesses were found in all ceramics, the roughness decreased when the ceramics were polished except for IPS Empress ceramic. No correlation on the roughness and enamel wear were found.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
TeseToda.pdf (5.47 Mbytes)
Date de Publication
2005-03-11
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2019. Tous droits réservés.