Thèse de Doctorat
DOI
10.11606/T.23.2005.tde-03102005-095345
Document
Auteur
Nom complet
Patricia Moreira de Freitas
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2005
Directeur
Jury
Eduardo, Carlos de Paula (Président)
Cury, Altair Antoninha Del Bel
Marques, Marcia Martins
Novelli, Moacyr Domingos
Serra, Monica Campos
Titre en portugais
Estudo in vitro do efeito da irradiação com o laser de er,cr:ysgg na inibição do processo de desmineralização do esmalte dental
Mots-clés en portugais
Cr:YSGG
Desmineralização
Esmalte
Laser de Er
Microdureza
Mineral
Resumé en portugais
O crescente desenvolvimento e aprimoramento das técnicas e materiais odontológicos introduziu a tecnologia laser nas diversas especialidades da Odontologia. Ainda que existam poucos estudos na literatura quanto ao emprego do laser de Er,Cr:YSGG para o tratamento preventivo de lesões de cárie, acredita-se que a sua aplicação sobre a estrutura dental seja capaz de promover uma superfície mais resistente a desafios ácidos. O objetivo deste estudo foi avaliar o efeito da irradiação do esmalte dental humano com o laser de Er,Cr:YSGG, com diferentes densidades de energia, em relação à desmineralização. Quarenta e cinco blocos de esmalte dental de terceiros molares humanos (3 x 3 mm) foram aleatoriamente divididas em 5 grupos (n=9): G1 – Laser de Er,Cr:YSGG 0,25 W, 20 Hz, 2,84 J/cm 2 , G2 – – Laser de Er,Cr:YSGG 0,50 W, 20 Hz, 5,68 J/cm 2 , G3 – Laser de Er,Cr:YSGG 0,75 W, 20 Hz, 8,52 J/cm 2 , G4 – Tratamento com dentifrício fluoretado (controle positivo), G5 – Sem tratamento (controle negativo). Em seguida, as amostrasഊforam submetidas a ciclagem de pH por 2 semanas, permanecendo, diariamente, 6 h e 18 h nas soluções desmineralizante e remineralizante, respectivamente. Após o desafio ácido, as amostras foram seccionadas e o teste de Microdureza Knoop (25 g, 30 seg) foi realizado em distancias pré-determinadas em relação a superfície do esmalte (15 µm - 300 µm). OS valores de ANOVA e teste de Student Newman Keuls foram realizados(α =5%). Os percentuais de inibição de cárie encontrados foram de: G1- 36,64 %, G2-37,98 %. G3 – 63,83% e G4 – 50,47 %. Não houve diferenças estatisticamente significativas entre a porcentagem de volume mineral perdido nos grupos G1 (1391,81±521,65) e G2 (1291,90±656,49), porém ambos foram maiores do que o grupo G3 (753,32±287,07). Nenhum dos grupos submetidos ao tratamento com o laser de Er,Cr:YSGG diferiu estatisticamente do grupo controle positivo (G4). Os resultados deste estudo in vitro sugerem que a irradiação com o Laser de Er,Cr:YSGG com densidade de energia de 8,52 J/cm 2 pode ser uma alternativa efetiva na obtenção do aumento da resistência ácida do esmalte e que densidades de energia menores podem apresentar um potencial cariostático semelhante ao tratamento com dentifrício fluoretado.
Titre en anglais
In vitro study of the effect of ER,CR:YSGG Laser irradiation on theinhibition of enamel demineralization
Mots-clés en anglais
Cr:YSGG Laser
Demineralization
ER
Microhardness
Mineral
Rnamel
Resumé en anglais
The continuing development and improvement of the techniques and materials have introduced the laser technology in the different specialties of Dentistry. Even though there are still few studies on the use of the Er,Cr:YSGG Laser on caries prevention, one believes that the enamel irradiation with this wavelength can lead to a more acid resistant surface. The aim of the present study was to evaluate the effect of different parameters of the Er,Cr:YSGG Laser irradiation on the enamel mineral loss. Forty five enamel samples obtained from third molars (3 x 3 mm) were randomly divided in 5 groups (n=9): G1 – Er,Cr:YSGG Laser 0.25 W, 20 Hz, 2.84 J/cm 2 , G2 – Er,Cr:YSGG Laser 0.50 W, 20 Hz, 5.68 J/cm 2 , G3 – Er,Cr:YSGG Laser 0.75 W, 20 Hz, 8.52 J/cm 2 , G4 – Treatment with fluoride toothpaste (positive control), G5 – No treatment (negative control). After the surface treatment, the samples were submitted to a 2-weeks pH-cycling, consisted of the daily immersion in demineralizing and remineralizing solutions for 6 h e 18 h, respectively. Afterഊthe acid challenge, the samples were sectioned and the Knoop microhardness test was performed (25 g, 30 sec) at different depth from the enamel surface (15 µm - 300 µm). ANOVA and Student Newman Keuls tests were performed (α =5%). The percentage of lesion inhibition for each group was: G1- 36.64 %, G2- 37.98 %. G3 – 63.83% e G4 – 50.47 %. Regarding the percentage of mineral loss volume, Groups G1 (1391.81±521.65) and G2 (1291.90±656.49) did not differ from each other, but both were higher than group G3 753.32±287.07). All the groups irradiated with the Er,Cr:YSGG were similar to the positive control group (G4). The findings of the present study suggest that the Er,Cr:YSGG laser at 8.52 J/cm 2 can be an alternative for the enhancement of enamel acid resistant and that lower energy densities seem to present a cariostatic potential comparable to the use of fluoride dentifrice.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2005-10-14
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
Centro de Informática de São Carlos
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2020. Tous droits réservés.