Disertación de Maestría
DOI
10.11606/D.23.2009.tde-08042009-154024
Documento
Autor
Nombre completo
Simone Gonçalves Moretto
Dirección Electrónica
Instituto/Escuela/Facultad
Área de Conocimiento
Fecha de Defensa
Publicación
São Paulo, 2009
Director
Tribunal
Freitas, Patricia Moreira de (Presidente)
Aranha, Ana Cecilia Corrêa
Reis, André Figueiredo
Título en portugués
Análise morfológica e da resistência de união da superfície dentinária irradiada com os lasers de Er:YAG e Er,Cr:YSGG
Palabras clave en portugués
Cr:YSGG
Dentina
Laser de Er
Laser de Er:YAG
Microscopia Eletrônica de Transmissão
Microscopia Eletrônica de Varredura
Microtração
Resistência de união
Resumen en portugués
Avanços na tecnologia introduziram o laser como um grande aliado na remoção seletiva do tecido cariado. Entretanto, o efeito dos lasers e seus diferentes parâmetros nos tecidos duros dentais e fibrilas colágenas não foi completamente estudado. O objetivo deste estudo foi avaliar os efeitos da irradiação com os lasers de Er:YAG e Er,Cr:YSGG na morfologia e na resistência de união da dentina irradiada à resina composta. Sessenta e quatro hemi-discos de dentina obtidos de terceiros molares humanos foram aleatoriamente divididos em 9 grupos (n=7): G1 Controle (não irradiado); G2 Laser de Er:YAG 250 mJ, 4 Hz; G3 Laser de Er:YAG 200 mJ, 4 Hz; G4 Laser de Er:YAG 180 mJ, 10 Hz; G5 Laser de Er:YAG 160 mJ, 10 Hz; G6 - Laser de Er,Cr:YSGG 2W, 20 Hz; G7 - Laser de Er,Cr:YSGG 2,5W, 20 Hz; G8 - Laser de Er,Cr:YSGG 3W, 20 Hz; G9 - Laser de Er,Cr:YSGG 4W, 20 Hz. Destes, vinte e sete amostras (n=3) foram processadas e destinadas à avaliação em Microscopia Eletrônica de Varredura (MEV) para análise morfológica de superfície e em corte transversal da dentina irradiada. Nove fragmentos (n=1) foram submetidos à Microscopia Eletrônica de Transmissão (MET) e vinte e sete (n=3) foram restaurados para análise da interface adesiva. Para o teste de resistência de união, 45 superfícies dentinárias planificadas foram restauradas e, após 24 horas de armazenamento em água, foram submetidas ao teste de microtração. O teste de ANOVA (=5%) foi realizado e verificou-se que o G1 apresentou os maiores valores de resistência de união quando comparado aos demais grupos experimentais. Não houve diferença estatisticamente significativa entre os grupos irradiados, e a análise morfológica revelou para estes grupos uma superfície irregular, com aparência escamosa, sem smear layer e com os túbulos dentinários abertos. Nos cortes transversais foi possível observar que esses efeitos se estendem à subsuperfície dentinária e resultam na formação de um padrão modificado dos tags durante o processo de hibridização. Os resultados deste estudo in vitro sugerem que a irradiação com os lasers de Er:YAG e Er,Cr:YSGG promovem um padrão morfológico específico da superfície dentinária, os quais podem interferir negativamente nos valores de resistência de união à resina composta.
Título en inglés
Morphological analysis and micro-tensile bond strength of dentin surface irradiated with Er:YAG and Er,Cr:YSGG lasers
Palabras clave en inglés
Bond strength.
Cr:YSGG Laser
Dentin
Er
Er:YAG Laser
Scanning Electron Microscopy
Transmission Electron Microscopy
Resumen en inglés
Improvements on technology have introduced the laser as a great ally in the selected removal of dental caries. However, the different laser parameters and their effects on dental hard tissues and collagen fibrils have not yet been completely studied. The aim of the present study was to evaluate the effect of Er:YAG and Er,Cr:YSGG laser irradiation on dentin morphology and on microtensile bond strength of resin composite to the irradiated dentin. Sixty-four dentin hemi-disks obtained from sound human third molars were randomly divided into 9 groups (n=7): G1 Control, G2 Er:YAG Laser 250 mJ, 4 Hz; G3 Er:YAG Laser 200 mJ, 4 Hz; G4 Er:YAG Laser 180 mJ, 10 Hz; G5 Er:YAG Laser 160 mJ, 10 Hz; G6 - Er,Cr:YSGG Laser 2W, 20 Hz; G7 - Er,Cr:YSGG Laser 2,5W, 20 Hz; G8 - Er,Cr:YSGG Laser 3W, 20 Hz; G9 - Er,Cr:YSGG Laser 4W, 20 Hz. Twenty seven specimens (n=3) were processed for Scanning Electron Microscopy (SEM) for surface and cross-sectional morphological analysis. Nine specimens (n=1) were processed for Transmission Electron Microscopy (TEM) and twenty seven (n=3) were restored to evaluate the adhesive interface. For the microtensile bond strength (^TBS) test, 45 flat occlusal dentin surfaces were restored and after storage in water for 24h, were submitted to ^TBS test. ANOVA (=5%) showed that G1 (control group) presented the highest ^TBS values when compared with the irradiated groups, which did not differ from each other. SEM analysis showed an irregular scaly surface, free of smear layer and with open dentinal tubules. The cross-sectional dentin micrographs showed that the effects of laser extended to the dentin subsurface resulting in a pattern of tags modified in the hibridization process. The findings of this in vitro study showed that both Er:YAG and Er,Cr:YSGG laser irradiation resulted in a specific morphological pattern of dentin that negatively affects the bond strength to resin composite to such dentin.
 
ADVERTENCIA - La consulta de este documento queda condicionada a la aceptación de las siguientes condiciones de uso:
Este documento es únicamente para usos privados enmarcados en actividades de investigación y docencia. No se autoriza su reproducción con finalidades de lucro. Esta reserva de derechos afecta tanto los datos del documento como a sus contenidos. En la utilización o cita de partes del documento es obligado indicar el nombre de la persona autora.
Fecha de Publicación
2009-06-08
 
ADVERTENCIA: Aprenda que son los trabajos derivados haciendo clic aquí.
Todos los derechos de la tesis/disertación pertenecen a los autores
Centro de Informática de São Carlos
Biblioteca Digital de Tesis y Disertaciones de la USP. Copyright © 2001-2020. Todos los derechos reservados.