Doctoral Thesis
DOI
10.11606/T.23.2012.tde-13042013-105219
Document
Author
Full name
Frederico Seidi Hori
E-mail
Institute/School/College
Knowledge Area
Date of Defense
Published
São Paulo, 2012
Supervisor
Committee
Carvalho, Rubens Corte Real de (President)
Andrade, Alessandra Pereira de
Kawano, Yoshio
Santos, Flávio Augusto Merichello dos
Turbino, Miriam Lacalle
Title in Portuguese
Resistência de união e análise quantitativa da camada híbrida através de espectroscopia micro-Raman de quatro sistemas adesivos
Keywords in Portuguese
Adesão
Camada híbrida
Micro-Raman
Abstract in Portuguese
Adesivos de frasco único, tanto auto-condicionantes como condicione-e-lave, são misturas complexas de monômeros resinosos hidrofílicos e hidrofóbicos dissolvidos em combinações de água/solvente.Embora a inclusão de monômeros hidrofílicos tenha conseguido altas forças de adesão imediata, estudos têm mostrado que a interface resina-dentina têm se tornado muito mais fraca através do tempo. Nesse estudo através da microtração, avaliamos a resistência adesiva de 4 sistemas adesivos e através da espectroscopia micro-Raman analisamos quantitativamente a camada híbrida formada por esses adesivos. Para a microtração, os fatores de variação foram 2: o tipo de adesivo (AdperScotchbondMulti-Purpose, AdperSingle Bond 2, Adper SE Plus, AdperEasyOne), e o período de armazenamento, em 3 níveis (1 dia, 30 dias, 180 dias), totalizando 12 níveis de variação. As unidades experimentais foram confeccionadas sobre 120 superfícies de dentina de terceiros molares humanos hígidos e não irrompidos (n= 10).Para análise estatística foi utilizado o teste paramétrico de análise de variância ANOVA e o teste de múltipla comparação de Games Howell.Para a espectroscopia micro-Raman foram utilizados 3 dentes para cada sistema adesivo, totalizando 12 dentes (n=3).Os espectros Raman dos espécimes foram registrados num espectrômetro Micro-Raman RENISHAW InVia com excitação em 785 nm (laser de diodo, RENISHAW) acoplado a um microscópio LEICA DM2500M, com estágio motorizado (x;y;z)RENISHAW MS 20 EncodedStage com resoluções lateral e axial de 100 nm e 1 m. Os adesivos condicione-e-lave ScotchbondMulti-Purpose e SingleBonddesse estudo apresentaram os maiores valores de resistência adesiva, apresentando valores dentro de uma faixa de 44,36 a 50,66 MPa, enquanto que os adesivos AdperSE e Easy One apresentaram valores de 17,97 a 24,60 MPa. O adesivo que apresentou os maiores valores de resistência adesiva foi o ScotchbondMulti-Purpose e o que teve o pior desempenho foi o adesivo Easy One. Todos os adesivos apresentaram queda significativa de resistência de união após 30 e 180 dias. Na análise micro- Raman, o adesivo ScotchbondMulti-Purpose mostrou-se mais homogêneo e com valores de penetração do adesivo semelhantes aos do Single Bond e do Easy One. O adesivo SE Plus apresentou a menor penetração do adesivo e a camada híbrida mais fina. Concluímos neste trabalho que avaliando 4 diferentes tipos de adesivos de uma mesma marca, existe uma relação negativa entre as estratégias de adesão (diminuição do número de passos e frascos) e a resistência de união e a qualidade da camada híbrida.
Title in English
Bond Strength and quantitative analysis of the hybrid layer by micro-Raman spectroscopy of four adhesive systems
Keywords in English
Adhesion
Hybrid layer
Micro-Raman
Abstract in English
One-bottle adhesives, both self-etching as etch-and-rinse, are complex mixtures of hydrophilic and hydrophobic monomers resin combinations dissolved in water / solvent. Although the inclusion of hydrophilic monomers has achieved high immediate adhesion forces, studies have shown that dentin-resin interface have become much weaker over time. In this study, bond strength of four adhesive systems was evaluated bymicrotensile test and quantitative analyze ofthe hybrid layer was obtained by micro-Raman spectroscopy. For microtensile test, the factors of variation were 2: the type of adhesive (AdperScotchbondMulti-Purpose, AdperSingle Bond 2, Adper SE Plus, AdperEasy One), and the period of storage at 3 levels (1 day, 30 days, 180 days), totaling 12 levels of variation. The experimental units were made on 120 dentin surfaces of intact humanunerupted third molars (n = 10). The parametric analysis of variance ANOVA and multiple comparison Games Howell was used for statistical analysis. For micro-Raman spectroscopy were used three teeth for each adhesive system, with a total of 12 teeth (n = 3). Raman spectra of the samples were recorded on a Micro-Raman spectrometer RENISHAW invia with 785 nm excitation (laser diode, RENISHAW) coupled to a microscope LEICA DM2500M with motorized stage (x, y, z) RENISHAW MS 20 EncodedStage with lateral and axial resolutionof 100 nm and 1 microns. Etch-and-rinse adhesives ScotchbondMulti-Purposeand SingleBond of this study showed the highest bond strength values, with values within a range from 44.36 to 50.66 MPa, whereas the self-etch adhesives SE Plusand Easy One had values of 17.97 to 24.60 MPa. The adhesive that showed the highest bond strength was ScotchbondMulti-Purpose and the worst performance was fromEasy One.All adhesives showed a significant decrease in bond strength after 30 and 180 days. In micro-Raman analysis, the ScotchbondMulti-Purpose was more homogeneous and had penetration values similar to those of the adhesive Single Bond and Easy One. The SE Plus had the lowest penetration of the adhesive and the thinner hybrid layer. We conclude that evaluating 4 different types of adhesives of the same brand, there is a negative relationship between the strategies of adhesion (decreasing the number of steps and bottles) and bond strength and quality of the hybrid layer.
 
WARNING - Viewing this document is conditioned on your acceptance of the following terms of use:
This document is only for private use for research and teaching activities. Reproduction for commercial use is forbidden. This rights cover the whole data about this document as well as its contents. Any uses or copies of this document in whole or in part must include the author's name.
Publishing Date
2013-05-27
 
WARNING: Learn what derived works are clicking here.
All rights of the thesis/dissertation are from the authors
Centro de Informática de São Carlos
Digital Library of Theses and Dissertations of USP. Copyright © 2001-2019. All rights reserved.