Thèse de Doctorat
DOI
https://doi.org/10.11606/T.23.2012.tde-13042013-123740
Document
Auteur
Nom complet
Simone Gonçalves Moretto
Adresse Mail
Unité de l'USP
Domain de Connaissance
Date de Soutenance
Editeur
São Paulo, 2012
Directeur
Jury
Freitas, Patricia Moreira de (Président)
Cardoso, Marcio Vivan
Giannini, Marcelo
Matos, Adriana Bona
Zezell, Denise Maria
Titre en portugais
Estudo longitudinal da resistência e qualidade de união de diferentes sistemas adesivos à dentina irradiada com laser de femtossegundos
Mots-clés en portugais
Dentina
Laser de Femtossegundos
Microscopia Eletrônica de Transmissão
Microscopia Eletrônica de Varredura
Nanoinfiltração
Resistência de união
Sistemas adesivos
Resumé en portugais
Recentemente, os lasers de pulsos ultracurtos têm sido avaliados para o preparo dos tecidos duros dentais devido à sua habilidade de reduzir os efeitos térmicos resultantes da irradiação. O objetivo deste estudo foi avaliar a efetividade de união de 3 sistemas adesivos à dentina preparada com o laser de femtossegundos (10-15 s). Para isso, 60 terceiros molares foram preparados com o laser de femtossegundos (1.450 nm; 0,3W; 100.000Hz) ou ponta diamantada, divididos em 3 subgrupos (n=10) restaurados utilizando o adesivo condicione e lave de 3 passos Optibond FL (OFL; Kerr), o autocondicionante de 2 passos Clearfil SE (CSE; Kuraray) ou o autocondicionante de 1 passo G-aenial Bond (GAB; GC). Após 1 semana de armazenamento em água, os dentes foram seccionados (1,0x1,0 mm) e testados imediatamente e após 6 meses de armazenamento. Vinte e quatro amostras adicionais foram preparadas com o laser ou ponta diamantanda conforme descrito acima. Seis amostras foram seccionadas em espécimes menores e aleatoriamente preparados para observação das características morfológicas da superfície (n=3) e subsuperfície (n=3) em Microscópio Eletrônico de Varredura (MEV) (n=3) e Microscopia Eletrônica de Transmissão (MET) (n=3). As outras 18 amostras foram restauradas com os sistemas adesivos supramencionados, seccionados em espécimes menores e distribuídos para avaliação da interface adesiva em MEV (n=3) e padrão de nanoinfiltração após 1 semana (n=2) e 6 meses (n=2) em MET. O modelo linear de efeitos mistos (=0,05) revelou um efeito significante dos fatores adesivo, armazenagem e a interação preparo x armazenagem na resistência de união. Todos os adesivos apresentaram uma redução significante da resistência de união após 6 meses de armazenamento (p<0,0001) para ambos os tipos de preparo. Com relação ao sistema adesivo, a única diferença verificada foi o maior valor de resistência de união do GAB quando aplicado sobre as superfícies irradiadas (56,71±10,72 MPa) quando comparadas com as preparadas com ponta diamantada (43,14±14,93 MPa) após 1 semana de armazenamento. A análise de fratura revelou fraturas mistas, adesivas e coesivas em dentina para ambos os métodos de preparo com um discreto aumento do número de fraturas mistas após 6 meses de armazenamento exceto para o GAB, que apresentou principalmente fraturas adesivas e mistas. A análise em MEV revelou uma fina camada de debris sobre a superfície da dentina irradiada e a hibridização com todos os sistemas adesivos resultou num íntimo contado da interface adesiva com o substrato. A análise em MET da subsuperfície irradiada revelou fibrilas colágenas preservadas. A análise da interface adesiva revelou um aumento dos depósitos de prata na camada híbrida para todos os adesivos, após 6 meses de armazenamento, independentemente do tipo de preparo. Apenas o GAB apresentou maiores depósitos de prata após 1 semana de armazenamento para as superfícies preparadas com ponta diamantada. A irradiação com o laser de femtossegundos não reduziu a receptividade da dentina aos sistemas adesivos, resultando em valores de resistência de união similares aos obtidos com a ponta diamantada; além de uma ótima interação do substrato com os sistemas adesivos e deposições de prata similares àquelas obtidas com a ponta diamantada.
Titre en anglais
Long term evaluation of bond strength and quality of the interface of different adhesive systems to femtosecond laser irradiated dentin
Mots-clés en anglais
Adhesive systems
Bond strength
Dentin
Femtosecond laser
Nanoleakage
Scanning Electron Microscopy
Transmission Electron Microscopy
Resumé en anglais
Recently, the applicability of ultrashort pulsed lasers has been studied for dental hard-tissue irradiation because of its reduced residual thermal damage. The aim of this study was to determine the bonding effectiveness of 3 contemporary adhesive systems to dentin prepared by femtosecond (10-15 sec) laser-irradiation. For this, 60 third molars were prepared either by the femtosecond laser (1450 nm; 0.3W; 100,000Hz) or by bur, randomly divided into 3 subgroups (n=10) and restored with a composite using either the 3-step etch-and-rinse adhesive Optibond FL (OFL; Kerr), the 2-step self-etch adhesive Clearfil SE (CSE; Kuraray) or the 1-step self-etch adhesive G-aenial Bond (GAB; GC). After 1-week water storage, the teeth were sectioned (1.0x1.0 mm) and half of the specimens were tested until failure using a micro-tensile bond-strength (TBS) approach. The other half was stored in water and tested after 6 months. Twenty-four additional dentin samples were exposed to the diamond bur and the laser, following the same abovementioned parameters. Three samples of each treatment were sectioned in smaller specimens in order to be characterized for surface (n=3) and cross-sectional morphological analysis using Scanning Electron Microscopy (SEM) (n=3) and Transmission Electron Microscopy (TEM) (n=3). The other eighteen samples were hybridized with the abovementioned adhesive systems, sectioned in smaller samples and distributed for evaluation of the interface under SEM (n=3) and nanoleakage distribution for 1 week (n=2) and 6 months (n=2) under TEM. Linear mixed effect model (=0.05) revealed a significant effect of the factors adhesive, storage and the interaction of preparation x storage on the TBS. All adhesives presented a significant reduction of the bond strength after 6-month storage (p<0.0001) for both preparation methods. Regarding the adhesive system, the only difference found was a significantly higher TBS of GAB to laser-irradiated (56.71±10.72 MPa) than to bur-cut dentin (43.14±14.93 MPa) after 1-week water storage. Fracture analysis showed mixed, adhesive and cohesive failures in dentin similarly for both preparation methods with a slightly increase of the mixed failures after 6-months water storage for OFL and CSE, but not for GAB that presented mainly adhesive and mixed failures. SEM disclosed a thin layer of debris on the laser-irradiated dentin surface and the hybridization with all adhesive systems resulted in a very tight interface. TEM analysis of the irradiated subsurface revealed collagen fibrils preserved and for the nanoleakage evaluation an increase of silver deposits at hybrid layer for all adhesives testes after 6-months water storage, irrespective of the preparation methods. Only the GAB presented great silver deposits even after 1-week water storage for the bur-cut preparation method. Femtosecond laser irradiation did not reduce the bonding receptiveness of dentin resulting in similar values obtained with the preparation by bur. Additionally it led to a great interaction with different adhesive systems and silver deposits comparable to those obtained with the bur-cut preparation method.
 
AVERTISSEMENT - Regarde ce document est soumise à votre acceptation des conditions d'utilisation suivantes:
Ce document est uniquement à des fins privées pour la recherche et l'enseignement. Reproduction à des fins commerciales est interdite. Cette droits couvrent l'ensemble des données sur ce document ainsi que son contenu. Toute utilisation ou de copie de ce document, en totalité ou en partie, doit inclure le nom de l'auteur.
Date de Publication
2013-05-27
 
AVERTISSEMENT: Apprenez ce que sont des œvres dérivées cliquant ici.
Tous droits de la thèse/dissertation appartiennent aux auteurs
CeTI-SC/STI
Bibliothèque Numérique de Thèses et Mémoires de l'USP. Copyright © 2001-2024. Tous droits réservés.